Phase evolutions of high energy ball milled Ni-66.7at% Si | |
Ji, Genhun; Ma, Qin; Guo, Tieming; Zhou, Qi; Jia, Jiangang; Chen, Xueding | |
2007 | |
关键词 | nickel silicide ball milling phase transitions x-ray diffraction |
卷号 | 336-338 |
页码 | 2325-+ |
英文摘要 | The high-energy ball milling of Ni-66.7 at% Si elemental powder mixtures was carried out using a FRITSCH Puluerisette-5 mill. XRD was used to identify the phase evolutions during high-energy ball milling. The XRD patterns showed that the intensities of nickel peaks and silicon peaks gradually decreased with milling time increased from 1 h to 10 h, simultaneously, the peaks of NiSi2 and NiSi appeared. With milling time further increased to 45 h, single phase of NiSi2 formed. New peaks were observed after 75 h milling, which were indexed as FeSi. This reveals that long time high-energy ball milling: will induce Fe contamination and that Fe exhibits greater activity and reacts with NiSi2 forming FeSi and NiSi. Moreover, the peaks intensity of FeSi and NiSi increased with milling time increased from 75 h to 180 h. The phase evolutions of Ni-66.7 at% Si during high energy ball milling were discussed. |
会议录 | HIGH-PERFORMANCE CERAMICS IV, PTS 1-3 |
会议录出版者 | TRANS TECH PUBLICATIONS LTD |
会议录出版地 | KREUZSTRASSE 10, 8635 DURNTEN-ZURICH, SWITZERLAND |
语种 | 英语 |
WOS研究方向 | Materials Science |
WOS记录号 | WOS:000246148002148 |
内容类型 | 会议论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/38162] |
专题 | 材料科学与工程学院 外国语学院 |
通讯作者 | Ji, Genhun |
作者单位 | Lanzhou Univ Technol, Minist Educ, Key Lab Nonferrous Metal Alloys, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Ji, Genhun,Ma, Qin,Guo, Tieming,et al. Phase evolutions of high energy ball milled Ni-66.7at% Si[C]. 见:. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论