Synthesis and properties of epoxy resin/graphite composites via in situ polymerization

doi:10.4028/www.scientific.net/AMR.415-417.358

	Synthesis and properties of epoxy resin/graphite composites via in situ polymerization
	Lu, Xuefeng; La, Peiqing; Guo, Xin; Wei, Yupeng
	2012
关键词	Epoxy resin Bending Strength Shore Hardness In Situ Polymerization
卷号	415-417
DOI	10.4028/www.scientific.net/AMR.415-417.358
页码	358-361
英文摘要	Synthesis and properties of epoxy resin/graphite composites via in situ condensation polymerization of monomers in the presence of graphite particles were investigated. The results showed graphite particles were well dispersed in the epoxy resin matrix. Shore hardness and bending strength varied with the amount of graphite, and they were all improved greatly by an optimal content of 17.44% (mass fraction). The bending strength was 22.4MPa and Shore hardness was 9.8 HD. A plastic deformation can be seen in the composite with the range of strain 0.6-0.8%. The fitted yield strength is about 20MPa.
会议录	ADVANCED MATERIALS, PTS 1-3
会议录出版者	TRANS TECH PUBLICATIONS LTD
会议录出版地	LAUBLSRUTISTR 24, CH-8717 STAFA-ZURICH, SWITZERLAND
语种	英语
WOS研究方向	Materials Science
WOS记录号	WOS:000309893300069
内容类型	会议论文
源URL	[http://119.78.100.223/handle/2XXMBERH/37117]
专题	材料科学与工程学院省部共建有色金属先进加工与再利用国家重点实验室
通讯作者	Lu, Xuefeng
作者单位	Lanzhou Univ Technol, State Key Lab Gansu Adv Nonferrous Met Mat, Lanzhou 730050, Gansu, Peoples R China
推荐引用方式 GB/T 7714	Lu, Xuefeng,La, Peiqing,Guo, Xin,et al. Synthesis and properties of epoxy resin/graphite composites via in situ polymerization[C]. 见:.