Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet | |
Luo Xiaomei2; Bi Guangli2; Jiang Jing2; Li Ming2; Li Rongguang1; Li Yuandong2; Ma Ying2; Hao Yuan2 | |
刊名 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA |
2016-02 | |
卷号 | 26期号:2页码:390-397 |
关键词 | Mg-Dy-Zn alloy microstructure texture LPSO phase compressive anisotropy |
ISSN号 | 1003-6326 |
DOI | 10.1016/S1003-6326(16)64127-4 |
英文摘要 | Compressive anisotropy of extruded Mg-2Dy-0.5Zn (mole fraction, %) alloy sheet was investigated. The alloy sheet was mainly composed of a-Mg, (Mg, Zn)(x)Dy phase and a large number of long period stacking ordered (LPSO) phases distributed along the extrusion direction. The compressive experimental results show that the alloy sheet exhibits an obvious compressive anisotropy. The compressive strength of the specimen in the extrusion direction (ED) is higher than those of the specimens in the transverse direction (TD) and 45 degrees inclined to the extrusion direction. The compressive yield strength (CYS), ultimate compressive strength (UCS) and compressive strain of the specimen in the ED are 274.65 MPa, 518.94 MPa and 12.93%, respectively. The compressive anisotropy is mainly attributed to the distribution of LPSO phase and formation of < 10 (1) over bar0 > // ED fiber texture in the deformed grains. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
CSCD记录号 | CSCD:5661751 |
出版者 | ELSEVIER SCIENCE BV |
WOS记录号 | WOS:000369696900008 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33789] |
专题 | 发展规划处 材料科学与工程学院 |
作者单位 | 1.School of Mechanical Engineering, Shenyang University of Chemical Technology, Shenyang, Liaoning 110142, China 2.Lanzhou University of Technology, State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals;;Key Laboratory of Nonferrous Metal alloys and Processing, Ministry of Education, Lanzhou, Gansu 730050, China |
推荐引用方式 GB/T 7714 | Luo Xiaomei,Bi Guangli,Jiang Jing,et al. Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2016,26(2):390-397. |
APA | Luo Xiaomei.,Bi Guangli.,Jiang Jing.,Li Ming.,Li Rongguang.,...&Hao Yuan.(2016).Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,26(2),390-397. |
MLA | Luo Xiaomei,et al."Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 26.2(2016):390-397. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论