Microstructure evolution and properties of Al/Al-Mg-Si alloy clad wire during heat treatment | |
Wang, Xiang1; Guan, Ren-guo1; Zhang, Yang1; Su, Ning1; Ji, Lian-ze1; Li, Yuan-dong2; Chen, Ti-jun2 | |
刊名 | APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING |
2016-06 | |
卷号 | 122期号:6 |
ISSN号 | 0947-8396 |
DOI | 10.1007/s00339-016-0150-4 |
英文摘要 | In this paper, heat treatment was carried out on Al/Al-Mg-Si alloy clad wire, and microstructure evolution and properties of Al/Al-Mg-Si alloy clad wire during heat treatment were investigated. During solution, contents of Mg and Si in inner matrix increased due to dissolution of primary Mg2Si, and they also increased in outer matrix because Mg and Si diffused across the interface. Tensile strength of the clad wire increased firstly and then decreased, and elongation continuously increased, while conductivity continuously decreased with the increase in solution time. In aging process, Mg2Si precipitated in both inner core and outer layer, and the content and average diameter of the precipitate increased with the increase in aging time. The content of precipitate was higher, and the average diameter was bigger in inner core. Tensile strength of the clad wire increased firstly and then decreased with the increase in aging time, and the elongation continuously decreased, while the conductivity continuously increased. The peak tensile strength of 202 MPa occurred at 8 h, when the corresponding elongation was 20 % and the conductivity reached 56.07 %IACS. Even tensile strength of the prepared clad wire approximately equaled to that of Al-0.5Mg-0.35Si alloy 203 MPa, the conductivity was obviously improved from 54.2 to 56.07 %IACS. |
资助项目 | Fundamental Research Funds for the Central Universities[N150204016] |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
出版者 | SPRINGER HEIDELBERG |
WOS记录号 | WOS:000377061300055 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33681] |
专题 | 发展规划处 材料科学与工程学院 |
通讯作者 | Guan, Ren-guo |
作者单位 | 1.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Xiang,Guan, Ren-guo,Zhang, Yang,et al. Microstructure evolution and properties of Al/Al-Mg-Si alloy clad wire during heat treatment[J]. APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING,2016,122(6). |
APA | Wang, Xiang.,Guan, Ren-guo.,Zhang, Yang.,Su, Ning.,Ji, Lian-ze.,...&Chen, Ti-jun.(2016).Microstructure evolution and properties of Al/Al-Mg-Si alloy clad wire during heat treatment.APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING,122(6). |
MLA | Wang, Xiang,et al."Microstructure evolution and properties of Al/Al-Mg-Si alloy clad wire during heat treatment".APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING 122.6(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论