Microstructure evolution and mechanical properties of AZ80 magnesium alloy during high-pass multi-directional forging | |
Zhang, Jinlong1,2,3; Xie, Hui1,2; Lu, Zhenlin3; Ma, Ying1,2; Tao, Shiping1,2; Zhao, Kun1,2 | |
刊名 | RESULTS IN PHYSICS |
2018-09 | |
卷号 | 10页码:967-972 |
关键词 | High-pass multi-directional forging AZ80 magnesium alloy Ultrafine grain Severe plastic deformation |
ISSN号 | 2211-3797 |
DOI | 10.1016/j.rinp.2018.08.028 |
英文摘要 | Severe plastic deformation (SPD) was carried out on AZ80 alloy by high-pass multi-directional forging (MDF). Results showed that AZ80 alloy was effectively refined through MDF, and average grain size was refined to 0.73 mu m after 24 passes of forging. Its tensile strength, yield strength and elongation reached 333.8 MPa, 233.7 MPa and 17.8%, respectively, which were 1.22 times, 1.35 times and 2.54 times of those before the forging. When the MDF was less than 6 passes, the coarse grains were mechanically divided and refined, and a small amount of recrystallized grains appeared in the deformation band and its cross zone. When the MDF was more than 6 passes, grain division, recrystallization nucleation and grain growth occurred simultaneously, the microstructure refinement was slowed, and the uniformity was improved continuously. The heating between forging passes mainly caused restoration in the early forging, and the static recrystallization refinement in the middle of forging. In the later stage of forging, the grain growth caused by static recrystallization and the grain refinement caused by the deformation canceled out, and the microstructure no longer continued to refine with the increase of the forging pass. |
资助项目 | Shaanxi Provincial Education Department[15JK1377] |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE BV |
WOS记录号 | WOS:000443868900145 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/32495] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Zhang, Jinlong; Xie, Hui |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China 2.Xian Aeronaut Univ, Sch Mat Engn, Xian 710077, Shaanxi, Peoples R China 3.Xian Univ Technol, Sch Mat Sci & Engn, Xian 710084, Shaanxi, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Jinlong,Xie, Hui,Lu, Zhenlin,et al. Microstructure evolution and mechanical properties of AZ80 magnesium alloy during high-pass multi-directional forging[J]. RESULTS IN PHYSICS,2018,10:967-972. |
APA | Zhang, Jinlong,Xie, Hui,Lu, Zhenlin,Ma, Ying,Tao, Shiping,&Zhao, Kun.(2018).Microstructure evolution and mechanical properties of AZ80 magnesium alloy during high-pass multi-directional forging.RESULTS IN PHYSICS,10,967-972. |
MLA | Zhang, Jinlong,et al."Microstructure evolution and mechanical properties of AZ80 magnesium alloy during high-pass multi-directional forging".RESULTS IN PHYSICS 10(2018):967-972. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论