Reduction and direct alloying of calcium vanadate

CORC > 过程工程研究所 > 中国科学院过程工程研究所 > 研究所（批量导入）

	Reduction and direct alloying of calcium vanadate
	Yuan, ZF ; Huang, WL ; Zhu, SY ; Liao, DH ; Hu, HF
刊名	STEEL RESEARCH
	2002-10-01
卷号	73 期号:10 页码:428-432
关键词	vanadium
ISSN号	0177-4832
其他题名	Steel Res.
中文摘要	Based on the reduction law of calcium vanadate, which was explored in the laboratory, the experiments were carried out during direct alloying with calcium vanadate in a high-frequency induction furnace with a capacity of 25 kg. The average recovery ratio of vanadium was 83.4%. The tests were also carried out for direct alloying with a briquette of calcium vanadate in a 0.5 t electric arc furnace and with cold-bound pellets of calcium vanadate in a ladle to smelt the low alloy steel with mass contents of about 0.1% vanadium. The recovery ratios of vanadium were 89.9% and 86.0%, respectively.
英文摘要	Based on the reduction law of calcium vanadate, which was explored in the laboratory, the experiments were carried out during direct alloying with calcium vanadate in a high-frequency induction furnace with a capacity of 25 kg. The average recovery ratio of vanadium was 83.4%. The tests were also carried out for direct alloying with a briquette of calcium vanadate in a 0.5 t electric arc furnace and with cold-bound pellets of calcium vanadate in a ladle to smelt the low alloy steel with mass contents of about 0.1% vanadium. The recovery ratios of vanadium were 89.9% and 86.0%, respectively.
WOS标题词	Science & Technology ; Technology
类目[WOS]	Metallurgy & Metallurgical Engineering
研究领域[WOS]	Metallurgy & Metallurgical Engineering
关键词[WOS]	VANADIUM
收录类别	SCI
原文出处	://WOS:000179050300002
语种	英语
WOS记录号	WOS:000179050300002
公开日期	2013-11-12
内容类型	期刊论文
版本	出版稿
源URL	[http://ir.ipe.ac.cn/handle/122111/5671]
专题	过程工程研究所_研究所（批量导入）
作者单位	1.Chinese Acad Sci, Inst Proc Engn, Multiphase React Lab, Beijing, Peoples R China 2.Panzhihua Iron & Steel Co, Inst Vanadium & Titanium, Panzhihua, Peoples R China
推荐引用方式 GB/T 7714	Yuan, ZF,Huang, WL,Zhu, SY,et al. Reduction and direct alloying of calcium vanadate[J]. STEEL RESEARCH,2002,73(10):428-432.
APA	Yuan, ZF,Huang, WL,Zhu, SY,Liao, DH,&Hu, HF.(2002).Reduction and direct alloying of calcium vanadate.STEEL RESEARCH,73(10),428-432.
MLA	Yuan, ZF,et al."Reduction and direct alloying of calcium vanadate".STEEL RESEARCH 73.10(2002):428-432.