Study of the preparation and mechanism of formation of hollow monodisperse polystyrene microspheres by SPG (Shirasu Porous Glass) emulsification technique | |
Ma, GH; Omi, S; Dimonie, VL; Sudol, ED; El-Aasser, MS | |
刊名 | JOURNAL OF APPLIED POLYMER SCIENCE
![]() |
2002-08-15 | |
卷号 | 85期号:7页码:1530-1543 |
关键词 | SPG membrane membrane emulsification suspension polymerization hollow polystyrene microspheres particle morphology |
ISSN号 | 0021-8995 |
其他题名 | J. Appl. Polym. Sci. |
中文摘要 | In a previous study, it was found that monodisperse polystyrene (PSt) hollow particles can be prepared under special conditions by combining a Shirasu Porous Glass (SPG) emulsification technique and subsequent suspension polymerization process. That is, a mixture of styrene (St), N,N-dimethylamino ethyl methacrylate (DMAEMA), hexadecane (HD), and initiator N,N'-azobis(2,4-dimethylvaleronitrile) (ADVN) was used as the dispersed phase in an aqueous phase containing poly(vinyl pyrrolidone) (PVP), sodium lauryl sulfate (SLS), and water-soluble inhibitor. The dispersed phase was created by pushing the oil phase through the uniform pores of an SPG membrane into the continuous phase to form uniform droplets. Then, the droplets were polymerized at 70degreesC. It has been puzzling that hollow microspheres were obtained only when sodium nitrite (NaNO2) was used as a water-soluble inhibitor, while one-hole particles were formed when hydroquinone (HQ) or diaminophenylene (DAP) was used. In this study, the mechanism of formation of the hollow microspheres was verified by measuring the variation of diameter, molecular weight distribution, and monomer conversion, and by observing morphological changes during the polymerization, as well as by changing the type and amount of hydrophilic monomer, and initiator. It was found that the diameter of the oil droplets decreased, and a large amount of secondary new particles formed immediately after polymerization started in the case of NaNO2, However, there was no such apparent behavior to be observed when HQ or DAP was used. It was determined that the hollow particles formed due to the rapid phase separation between PSt and HD, and as a consequence, a large amount of monomer diffused into the aqueous phase to form the secondary particles. Rapid phase separation confined the HD inside the droplets, a nonequilibrium morphology. On the other hand, one-hole particles, representing an equilibrium morphology, formed when the phase separation occurred slowly because a lot of monomer existed inside of the droplets to allow mobility of the PSt. The addition of DMAEMA allowed the hollow particles to be formed more easily by decreasing the interfacial tension between the copolymer and aqueous phase. (C) 2002 Wiley Periodicals, Inc. |
英文摘要 | In a previous study, it was found that monodisperse polystyrene (PSt) hollow particles can be prepared under special conditions by combining a Shirasu Porous Glass (SPG) emulsification technique and subsequent suspension polymerization process. That is, a mixture of styrene (St), N,N-dimethylamino ethyl methacrylate (DMAEMA), hexadecane (HD), and initiator N,N'-azobis(2,4-dimethylvaleronitrile) (ADVN) was used as the dispersed phase in an aqueous phase containing poly(vinyl pyrrolidone) (PVP), sodium lauryl sulfate (SLS), and water-soluble inhibitor. The dispersed phase was created by pushing the oil phase through the uniform pores of an SPG membrane into the continuous phase to form uniform droplets. Then, the droplets were polymerized at 70degreesC. It has been puzzling that hollow microspheres were obtained only when sodium nitrite (NaNO2) was used as a water-soluble inhibitor, while one-hole particles were formed when hydroquinone (HQ) or diaminophenylene (DAP) was used. In this study, the mechanism of formation of the hollow microspheres was verified by measuring the variation of diameter, molecular weight distribution, and monomer conversion, and by observing morphological changes during the polymerization, as well as by changing the type and amount of hydrophilic monomer, and initiator. It was found that the diameter of the oil droplets decreased, and a large amount of secondary new particles formed immediately after polymerization started in the case of NaNO2, However, there was no such apparent behavior to be observed when HQ or DAP was used. It was determined that the hollow particles formed due to the rapid phase separation between PSt and HD, and as a consequence, a large amount of monomer diffused into the aqueous phase to form the secondary particles. Rapid phase separation confined the HD inside the droplets, a nonequilibrium morphology. On the other hand, one-hole particles, representing an equilibrium morphology, formed when the phase separation occurred slowly because a lot of monomer existed inside of the droplets to allow mobility of the PSt. The addition of DMAEMA allowed the hollow particles to be formed more easily by decreasing the interfacial tension between the copolymer and aqueous phase. (C) 2002 Wiley Periodicals, Inc. |
WOS标题词 | Science & Technology ; Physical Sciences |
类目[WOS] | Polymer Science |
研究领域[WOS] | Polymer Science |
关键词[WOS] | METHACRYLATE) COMPOSITE MICROSPHERES ; MEMBRANE EMULSIFICATION ; POLYMER PARTICLES ; MORPHOLOGY DEVELOPMENT ; INTERFACIAL PHENOMENA ; EMULSION |
收录类别 | SCI |
原文出处 | |
语种 | 英语 |
WOS记录号 | WOS:000176210500021 |
公开日期 | 2013-11-12 |
内容类型 | 期刊论文 |
版本 | 出版稿 |
源URL | [http://ir.ipe.ac.cn/handle/122111/5632] ![]() |
专题 | 过程工程研究所_研究所(批量导入) |
作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, Natl Key Lab Biochem Engn, Beijing 100080, Peoples R China 2.Tokyo Univ Agr & Technol, Grad Sch Bi1oapplicat & Syst Engn, Koganei, Tokyo 1848588, Japan 3.Lehigh Univ, Inst Emul Polymers, Bethlehem, PA 18015 USA 4.Lehigh Univ, Dept Chem Engn, Bethlehem, PA 18015 USA |
推荐引用方式 GB/T 7714 | Ma, GH,Omi, S,Dimonie, VL,et al. Study of the preparation and mechanism of formation of hollow monodisperse polystyrene microspheres by SPG (Shirasu Porous Glass) emulsification technique[J]. JOURNAL OF APPLIED POLYMER SCIENCE,2002,85(7):1530-1543. |
APA | Ma, GH,Omi, S,Dimonie, VL,Sudol, ED,&El-Aasser, MS.(2002).Study of the preparation and mechanism of formation of hollow monodisperse polystyrene microspheres by SPG (Shirasu Porous Glass) emulsification technique.JOURNAL OF APPLIED POLYMER SCIENCE,85(7),1530-1543. |
MLA | Ma, GH,et al."Study of the preparation and mechanism of formation of hollow monodisperse polystyrene microspheres by SPG (Shirasu Porous Glass) emulsification technique".JOURNAL OF APPLIED POLYMER SCIENCE 85.7(2002):1530-1543. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论