Effects of reheating time on microstructure and tensile properties of SiCp/2024 Al-based composites fabricated using powder thixoforming | |
Li, Pu Bo; Chen, Ti Jun; Zhang, Su Qing | |
刊名 | Metals and Materials International
![]() |
2017 | |
卷号 | 23期号:1页码:193-201 |
关键词 | Coarsening Composite materials Fabrication Hot working Microstructure Rheocasting Silicon Silicon carbide Tensile strength Tensile testing |
ISSN号 | 15989623 |
DOI | 10.1007/s12540-017-6363-z |
英文摘要 | The present investigation addresses a new technology, named powder thixoforming, used to fabricate SiCp/2024 Al-based composites. The effects of reheating time on microstructure and mechanical properties have been studied. The results indicated that the quantity of liquid, the coarsening behavior of the primary particles, the subsequent plastic deformation occurring during thixoforging, and thus the resulting microstructural compactness and mechanical properties changed as a function of reheating time. The best comprehensive tensile properties of the composite, that is an ultimate tensile strength of 370 MPa and an elongation of 4.4%, were obtained after reheating for 80 min at 625 °C, which was an increase of 23.3% and a decrease of 57.7%, respectively, compared to the 2024 alloy thixoforged under the same conditions as the composite. The fracturing in the composites occurred through interconnecting cracked SiCp and debonded SiC/Al interfaces caused by a higher concentration of stress and a coalescence of microvoids. © 2017, The Korean Institute of Metals and Materials and Springer Science+Business Media Dordrecht. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | Korean Institute of Metals and Materials |
WOS记录号 | WOS:000392036700022 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/151330] ![]() |
专题 | 兰州理工大学 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Li, Pu Bo,Chen, Ti Jun,Zhang, Su Qing. Effects of reheating time on microstructure and tensile properties of SiCp/2024 Al-based composites fabricated using powder thixoforming[J]. Metals and Materials International,2017,23(1):193-201. |
APA | Li, Pu Bo,Chen, Ti Jun,&Zhang, Su Qing.(2017).Effects of reheating time on microstructure and tensile properties of SiCp/2024 Al-based composites fabricated using powder thixoforming.Metals and Materials International,23(1),193-201. |
MLA | Li, Pu Bo,et al."Effects of reheating time on microstructure and tensile properties of SiCp/2024 Al-based composites fabricated using powder thixoforming".Metals and Materials International 23.1(2017):193-201. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论