Microstructures and properties of friction stir welding joints for LF2 aluminum alloy | |
Wang, Xi-Jing; A, Rong; Guo, Rui-Jie; Han, Xiao-Hui | |
刊名 | Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals
![]() |
2004-10-01 | |
卷号 | 14期号:10页码:1705-1710 |
ISSN号 | 10040609 |
英文摘要 | The welding of 10 mm thick LF2 aluminum alloy in friction stir welding was investigated. The results show that thicker plate should be jointed at lower welding velocity and rotation speed, otherwise there would get the joint with huge tunnel defect. The highest strength joints that are equal to parent metal can be obtained at 9 mm/min of welding velocity, 950 r/min of rotational speed and 6230 W of input energy, which are regarded as the most ideal parameters under experimental welding conditions. There are the smallest size grains of 15 μm in weld nugget; Heat affected zone are composed of coarse grains and the largest size of heat affected zone microstructure is 28 μm; Thermomechanically affected zone consists of strippy structure which is 85 μm in length in some area. Average microhardness in weld nugget is equal to parent metal's, the most microhardness is HV95 and lower than parent metal's in the area near weld nugget. |
语种 | 中文 |
出版者 | Central South University of Technology, Changsha, China |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/150311] ![]() |
专题 | 兰州理工大学 |
作者单位 | Lab. of Adv. Non-ferrous Metal Mat., Lanzhou Univ. of Technol., Lanzhou 730050, China |
推荐引用方式 GB/T 7714 | Wang, Xi-Jing,A, Rong,Guo, Rui-Jie,et al. Microstructures and properties of friction stir welding joints for LF2 aluminum alloy[J]. Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,2004,14(10):1705-1710. |
APA | Wang, Xi-Jing,A, Rong,Guo, Rui-Jie,&Han, Xiao-Hui.(2004).Microstructures and properties of friction stir welding joints for LF2 aluminum alloy.Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,14(10),1705-1710. |
MLA | Wang, Xi-Jing,et al."Microstructures and properties of friction stir welding joints for LF2 aluminum alloy".Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals 14.10(2004):1705-1710. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论