Microstructure and mechanical properties of submerged arc welding filled with Ni wire dissimilar joints comprising SUS304 and Q245R | |
Zhang, Peng Xian; Zhao, Peng; Cui, Yan Quan | |
2014 | |
会议日期 | June 28, 2014 - June 29, 2014 |
会议地点 | Shanghai, China |
关键词 | Cracks Engineering technology Filling Mechanical properties Microstructure Nickel Submerged arc welding Welding Welds Elevated temperature Influence mechanism Micro-structure evolutions Microstructure and mechanical properties Ni wires Peak temperatures Quantitative parameters Transition widths |
卷号 | 936 |
DOI | 10.4028/www.scientific.net/AMR.936.1780 |
页码 | 1780-1785 |
英文摘要 | Aim at the issue that the bending crack is easy to generate inside dissimilar welded joint of low alloy steel and stainless steel, a new process of submerged arc welding filled with Ni wire is put forward. The influence mechanism of filling quantity of Ni wire to the joint of microstructure evolutions and mechanical properties is mainly explored based on the contrast test of non-filling Ni wire and three different filling speeds of Ni wire. The experiment results indicate that, the filling process of Ni wire supplies austenite forming element, and alters heat allocation process of molten pool. The filling quantity of Ni wire is the quantitative parameter, it is used to control the transition width between low alloy steel and weld metal, also to adjust the peak temperature and holding time at elevated temperature of molten pool. When the value of the filling quantity of Ni wire is determined, the problem of bending crack in the fusion zone of low alloy steel can be solved, and also the overheat damage can be eliminated. At the same time, the grains of weld metal and heat affected zone are refined. And on this basis the plasticity, toughness and microhardness of welded joint can be guaranteed. © (2014) Trans Tech Publications, Switzerland. |
会议录 | Advanced Materials Research
![]() |
会议录出版者 | Trans Tech Publications Ltd |
语种 | 英语 |
ISSN号 | 10226680 |
内容类型 | 会议论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/117286] ![]() |
专题 | 兰州理工大学 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China |
推荐引用方式 GB/T 7714 | Zhang, Peng Xian,Zhao, Peng,Cui, Yan Quan. Microstructure and mechanical properties of submerged arc welding filled with Ni wire dissimilar joints comprising SUS304 and Q245R[C]. 见:. Shanghai, China. June 28, 2014 - June 29, 2014. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论