Fracture test and analysis of notched bars fabricated from Q235 steel at room temperature | |
Wang, Wan-Zhen1,2; Liu, Wu-Feng2; Wang, Xin-Tang1 | |
2010 | |
会议日期 | November 19, 2010 - November 22, 2010 |
会议地点 | Xiangtan, China |
关键词 | Cracks Fracture testing Manufacture Mechanical engineering Stress analysis Tensile testing Constructional steel Elliptical fracture model Notched bar Room temperature Tensile tests Yield models |
卷号 | 34-35 |
DOI | 10.4028/www.scientific.net/AMM.34-35.1406 |
页码 | 1406-1414 |
英文摘要 | Tensile tests at room temperature were performed on 20 notched bars fabricated from constructional steel Q235 specified in Chinese National Standards. The effect of the notch radius, r, and that of the notch depth ratio, d/D, on the fracture model of the constructional steel is examined. The experimental results demonstrate that cracks initiate at the notched section. Specimens with a sharper notch radius (a smaller r) and a larger notch depth (a smaller d/D ratio) show poor ductility, but high fracture strength. The experimental data are further analyzed using an elliptical yield model together with an elliptical fracture model originally proposed by the first author. The stress field computed from the numerical procedure indicates that the crack initiation occurs at the center of the notched section which experiences the highest stress triaxiality ratio (om/oseq). As the stresses at the notched section reach the limiting values determined from the elliptical fracture model, macroscopic fracture failure in the notched bar occurs. © (2010) Trans Tech Publications. |
会议录 | Applied Mechanics and Materials |
会议录出版者 | Trans Tech Publications, P.O. Box 1254, Clausthal-Zellerfeld, D-38670, Germany |
语种 | 英语 |
ISSN号 | 16609336 |
内容类型 | 会议论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/116806] |
专题 | 兰州理工大学 土木工程学院 |
作者单位 | 1.Faculty of Architectural, Civil Engineering and Environment, Ningbo University, Ningbo 315211, China; 2.School of Civil Engineering, Lanzhou University of Technology, Lanzhou 730055, China |
推荐引用方式 GB/T 7714 | Wang, Wan-Zhen,Liu, Wu-Feng,Wang, Xin-Tang. Fracture test and analysis of notched bars fabricated from Q235 steel at room temperature[C]. 见:. Xiangtan, China. November 19, 2010 - November 22, 2010. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论