Effect of cooling rate on microstructure and properties of heat-treated Fe3Al intermetallics | |
Li, Ya Min1,2; Liu, Hong Jun1; Hao, Yuan1 | |
2011 | |
会议日期 | April 9, 2011 - April 11, 2011 |
会议地点 | Guilin, China |
关键词 | Aluminum
Fracture
Hardness
Heat treatment
Intermetallics
Manufacture
Microstructure
Molds
Silicates
Sodium
Tensile strength
After-heat treatment
Cooling rates
Fe |
卷号 | 189-193 |
DOI | 10.4028/www.scientific.net/AMR.189-193.3891 |
页码 | 3891-3894 |
英文摘要 | The casting Fe3Al intermetallics were solidified in sodium silicate sand mould and permanent mould respectively to get different cooling rates. After heat treatment (1000°C/15 h homogenizing annealing + furnace cooling followed by 600°C/1 h tempering + oil quenching), the microstructure and properties of Fe3Al intermetallics were investigated. The results show that the heat-treated Fe3Al intermetallics at higher cooling rate has finer grained microstructure than lower cooling rate, and the lattice distortion increases due to the higher solid solubility of the elements Cr and B at higher cooling rate. The tensile strength and hardness of the Fe3Al intermetallics at higher cooling rate are slightly higher also. However, the impact power of intermetallics at higher cooling rate is 67.5% higher than that at lower cooling rate, and the impact fracture mode is also transformed from intercrystalline fracture at lower cooling rate to intercrystallin+transcrystalline mixed fracture at higher cooling rate. © (2011) Trans Tech Publications. |
会议录 | Advanced Materials Research |
会议录出版者 | Trans Tech Publications, P.O. Box 1254, Clausthal-Zellerfeld, D-38670, Germany |
语种 | 英语 |
ISSN号 | 10226680 |
内容类型 | 会议论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/116177] |
专题 | 兰州理工大学 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.Key Laboratory of Non-ferrous Metal Alloys and Processing, Ministry of Education, Lanzhou University of Technology, Lanzhou, Gansu, 730050, China; 2.State Key Laboratory of Gansu Advanced Non-Ferrous Metal Materials, College of Materials Science and Engineering, Lanzhou University of Technology, 287 Langongping Road, Lan Zhou, 730050, China |
推荐引用方式 GB/T 7714 | Li, Ya Min,Liu, Hong Jun,Hao, Yuan. Effect of cooling rate on microstructure and properties of heat-treated Fe3Al intermetallics[C]. 见:. Guilin, China. April 9, 2011 - April 11, 2011. |