Microstructure and tribology properties of plasma sprayed Cu14Al4.5FeNiCe clad | |
Li, Wensheng; Liu, Yi; Wang, Zhiping; Lu, Yang | |
刊名 | Hanjie Xuebao/Transactions of the China Welding Institution
![]() |
2011-11-01 | |
卷号 | 32期号:11页码:17-20 |
关键词 | Aluminum alloys Austenitic stainless steel Cerium alloys Copper alloys Friction Microstructure Phase structure Plasma jets Plasma spraying Scanning electron microscopy Steel metallurgy Steel testing Tensile testing Tribology Wear of materials Wear resistance Carbon steel substrates Energy dispersion spectroscope Friction coefficients Interfacial bonding strength Lubrication condition Sprayed clad Tribology properties Wear mechanisms |
ISSN号 | 0253360X |
英文摘要 | A Cu14Al4.5FeNiCe clad was formed on 45 carbon steel by plasma spraying of Cu14Al4.5FeNiCe alloy powder which was prepared by water cooled gas atomizing. The morphologies and phase structures of the clad, and the intersection between the clad and the carbon steel were investigated by optical microscope, scanning electron microscope, energy dispersion spectroscope and X-ray diffraction analyzer. The interfacial bonding strength between the clad and the carbon steel substrate was measured by tensile test. Tribology properties of the sprayed clad against 304 stainless steel under no-lubrication condition were evaluated on an UMT-2MT tester. Results showed that the sprayed Cu14Al4.5FeNiCe clad combined firmly to the 45 carbon steel substrate in a metallurgy way with a surface hardness of HB 320. The clad was composed of (α+γ2), β' and K phases, in which K phase was dispersed into the matrix of (α+γ2) and β'. The clad presented a good anti-lubrication character with friction coefficient of 0.105 under the load of 40N (5.7 MPa). Friction coefficient of the Cu14Al4.5FeNiCe clad against 304 stainless steel increased slightly with load increasing. The clad exhibited a high wear-resistance to 304 stainless steel, wear rate of the clad increased smoothly with load. |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/111296] ![]() |
专题 | 兰州理工大学 |
作者单位 | State Key Laboratory of Advanced Nonferrous Materials, Lanzhou University of Science and Technology, Lanzhou 730050, China |
推荐引用方式 GB/T 7714 | Li, Wensheng,Liu, Yi,Wang, Zhiping,et al. Microstructure and tribology properties of plasma sprayed Cu14Al4.5FeNiCe clad[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2011,32(11):17-20. |
APA | Li, Wensheng,Liu, Yi,Wang, Zhiping,&Lu, Yang.(2011).Microstructure and tribology properties of plasma sprayed Cu14Al4.5FeNiCe clad.Hanjie Xuebao/Transactions of the China Welding Institution,32(11),17-20. |
MLA | Li, Wensheng,et al."Microstructure and tribology properties of plasma sprayed Cu14Al4.5FeNiCe clad".Hanjie Xuebao/Transactions of the China Welding Institution 32.11(2011):17-20. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论