Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling

doi:10.1007/s12540-018-0066-y

CORC > 兰州理工大学 > 兰州理工大学

	Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling
	Li, Z. N.1; Wei, F. A.2; La, P. Q.1; Ma, F. L.1
刊名	METALS AND MATERIALS INTERNATIONAL
	2018-05
卷号	24 期号:3 页码:633-643
关键词	Rolling Microstructure Tensile strength Dynamic recrystallization
ISSN号	1598-9623
DOI	10.1007/s12540-018-0066-y
英文摘要	Large dimensional bulk 316L stainless steels were prepared by aluminothermic reaction method and rolled at 973 K (700 A degrees C) with different deformation, the microstructures evolution and mechanical properties were characterized in detail. The results showed that the microstructure of casting steel consists of nanocrystalline/submicrocrystalline/microcrystalline austenite and submicrocrystalline ferrite. After rolling to thickness reduction of 30, 50 and 70%, the submicrocrystalline austenite grains were crushed and dispersed more uniformly in the matrix of the steel, the grain size of submicrocrystalline austenite decreased from 246 to 136 nm. The mechanical properties of the rolled steels were significantly enhanced, with the thickness reduction increased from 30 to 70%, the tensile strength increased from 632 to 824 MPa, the yield strength increased from 425 to 615 MPa, and the elongation increased from 11 to 24%. After rolling to thickness reduction of 70%, the optimized combination of high strength and high ductility was obtained.
资助项目	National Natural Science Foundation of China[51561020]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	KOREAN INST METALS MATERIALS
WOS记录号	WOS:000431506500021
状态	已发表
内容类型	期刊论文
源URL	[http://119.78.100.223/handle/2XXMBERH/32667]
专题	兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室
通讯作者	La, P. Q.
作者单位	1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China 2.Qinghai Univ, Qinghai Prov Key Lab New Light Alloys, Qinghai Prov Engn, Res Ctr High Performance Light Met Alloys & Formi, Xining 810016, Qinghai, Peoples R China
推荐引用方式 GB/T 7714	Li, Z. N.,Wei, F. A.,La, P. Q.,et al. Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling[J]. METALS AND MATERIALS INTERNATIONAL,2018,24(3):633-643.
APA	Li, Z. N.,Wei, F. A.,La, P. Q.,&Ma, F. L..(2018).Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling.METALS AND MATERIALS INTERNATIONAL,24(3),633-643.
MLA	Li, Z. N.,et al."Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling".METALS AND MATERIALS INTERNATIONAL 24.3(2018):633-643.