Gas sensing selectivity of oxygen-regulated SnO2 films with different microstructure and texture | |
Li, Ruiwu1; Zhou, Yanwen1; Sun, Maolin1; Gong, Zhen1; Guo, Yuanyuan1; Yin, Xitao1; Wu, Fayu1; Ding, Wutong2 | |
刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
![]() |
2019-10 | |
卷号 | 35期号:10页码:2232-2237 |
关键词 | Gas sensor SnO2 Oxygen regulation Preferred orientation H-2 selectivity |
ISSN号 | 1005-0302 |
DOI | 10.1016/j.jmst.2019.06.005 |
英文摘要 | The selectivity of gas sensing materials is increasingly important for their applications. The oxygen-regulated SnO2 films with (110) and (101) preferred orientation were obtained through magnetron sputtering, followed by annealing treatment. Their micro-structure, surface morphology and gas response were investigated by advanced structural characterization and property measurement. The results showed that the as-prepared (110)-oriented SnO2 film was oxygen-rich and had more adsorption sites while the as-prepared (101)-oriented SnO2 film was oxygen-poor and more sensitive to de-oxidation. H-2 gas sensitivity, response speed, selectivity between H-2 and CO of the (110)-orientated SnO2 film was superior to that of the (101)-orientated SnO2 film. After treated at high temperature and high vacuum, the reduction of gas-sensing properties of the annealed (110) SnO2 film was much more than that of the annealed (101) SnO2 film. The lattice oxygen was responsible for the difference in gas-sensing response between (110) and (101)-oriented SnO2 films under oxygen regulation. This work indicated the gassensing selectivity of the different crystal planes in SnO2 film, providing a significant reference for design and extension of the related materials. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
资助项目 | Natural Science Foundation of Liaoning Province[20180550802] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | JOURNAL MATER SCI TECHNOL |
WOS记录号 | WOS:000484531600016 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/31536] ![]() |
专题 | 兰州理工大学 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Yin, Xitao; Wu, Fayu |
作者单位 | 1.Univ Sci & Technol Liaoning, Sch Mat Sci & Met, Anshan 114051, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Ruiwu,Zhou, Yanwen,Sun, Maolin,et al. Gas sensing selectivity of oxygen-regulated SnO2 films with different microstructure and texture[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(10):2232-2237. |
APA | Li, Ruiwu.,Zhou, Yanwen.,Sun, Maolin.,Gong, Zhen.,Guo, Yuanyuan.,...&Ding, Wutong.(2019).Gas sensing selectivity of oxygen-regulated SnO2 films with different microstructure and texture.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(10),2232-2237. |
MLA | Li, Ruiwu,et al."Gas sensing selectivity of oxygen-regulated SnO2 films with different microstructure and texture".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.10(2019):2232-2237. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论