Evaluation of Hydrogen Permeation into High-Strength Steel during Corrosion in Different Marine Corrosion Zones | |
Xu, Yong1,2,3,4; Huang, Yanliang1,2,3; Cai, Fanfan1,2,3,4; Wang, Zhengquan1,2,3,4; Lu, Dongzhu1,2,3; Wang, Xiutong1,2,3; Yang, Lihui1,2,3 | |
刊名 | APPLIED SCIENCES-BASEL |
2022-03-01 | |
卷号 | 12期号:6页码:20 |
关键词 | high-strength steel hydrogen permeation sensor marine corrosion environments |
DOI | 10.3390/app12062785 |
通讯作者 | Huang, Yanliang(hyl@qdio.ac.cn) |
英文摘要 | Hydrogen permeation into high-strength steel during the corrosion process can deteriorate their mechanical properties, thus seriously threatening the safety of steel structures. However, the hydrogen permeation behavior of steels in corrosive marine environments is not well understood. In this study, the hydrogen permeation behavior and mechanism of AISI 4135 steel in different marine corrosion zones was investigated for the first time using an in situ hydrogen permeation monitoring system via outdoor and indoor tests. The three-month outdoor hydrogen permeation test showed that the diffusible hydrogen content of the steels exposed to the marine atmospheric, splash, tidal and immersion zone was 3.15 x 10(-3), 7.00 x 10(-2), 2.06 x 10(-2) and 3.33 x 10(-2) wt ppm, respectively. Meanwhile, results showed that the hydrogen permeation current density was positively correlated with the corrosion rate of the steel in the marine environments. This research is of great significance for guiding the safe application of high-strength steel in the marine environments. |
资助项目 | National Natural Science Foundation of China[41976033] |
WOS研究方向 | Chemistry ; Engineering ; Materials Science ; Physics |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000776081300001 |
内容类型 | 期刊论文 |
源URL | [http://ir.qdio.ac.cn/handle/337002/178636] |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
通讯作者 | Huang, Yanliang |
作者单位 | 1.Pilot Natl Lab Marine Sci & Technol, Open Studio Marine Corros & Protect, Qingdao 266237, Shandong, Peoples R China 2.Chinese Acad Sci, Inst Oceanol, CAS Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China 3.Chinese Acad Sci, Ctr Ocean Megasci, 7 Nanhai Rd, Qingdao 266071, Peoples R China 4.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Xu, Yong,Huang, Yanliang,Cai, Fanfan,et al. Evaluation of Hydrogen Permeation into High-Strength Steel during Corrosion in Different Marine Corrosion Zones[J]. APPLIED SCIENCES-BASEL,2022,12(6):20. |
APA | Xu, Yong.,Huang, Yanliang.,Cai, Fanfan.,Wang, Zhengquan.,Lu, Dongzhu.,...&Yang, Lihui.(2022).Evaluation of Hydrogen Permeation into High-Strength Steel during Corrosion in Different Marine Corrosion Zones.APPLIED SCIENCES-BASEL,12(6),20. |
MLA | Xu, Yong,et al."Evaluation of Hydrogen Permeation into High-Strength Steel during Corrosion in Different Marine Corrosion Zones".APPLIED SCIENCES-BASEL 12.6(2022):20. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论