Facile Synthesis of Gold-nanoparticles-decorated Polymer Assemblies and Core-Shell Gold Nanoparticles Using Pluronic Block Copolymers | |
Shou QH(寿庆辉); Guo C(郭晨); Gao HS(高红帅); Zhou HC(周华从); Liu CC(刘春朝); Liu HZ(刘会洲) | |
刊名 | 过程工程学报
![]() |
2011 | |
卷号 | 11.0期号:004页码:711 |
ISSN号 | 1009-606X |
英文摘要 | Synthesis of gold nanoparticles (AuNPs) and Pluronic triblock copolymer composite in aqueous medium was studied. Gold-polymer nanocomposite with different structures was fabricated by tailoring the molar ratio of gold precursors to Pluronic P123 molecules or pH value of the P123 solution. When a lower volume ratio of AuC14-/P123 (0.05) was employed at pH 11.1, a nanostmcture similar to plum pudding was obtained. AuNPs with an average diameter of 13.1 nm were embedded in Pluronic assemblies, and each one held about 21 single gold nanoparticles. When AuCln-/P123 was increased to 0.1, core-shell structure was obtained if the pH value was in the range of 10.6-11.6, while gold polyhedra were fabricated when pH value was 8.1. Typical core-shell AuNPs had an average diameter of 9.6 nm with a narrow size distribution, while gold polyhedras with a mean diameter of 12.8 nm was obtained. The specific morphologies of the resultant nanocomposite were presumably obtained due to the synergistic interaction among the reactants. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.ipe.ac.cn/handle/122111/47421] ![]() |
专题 | 中国科学院过程工程研究所 |
作者单位 | 中国科学院过程工程研究所 |
推荐引用方式 GB/T 7714 | Shou QH,Guo C,Gao HS,et al. Facile Synthesis of Gold-nanoparticles-decorated Polymer Assemblies and Core-Shell Gold Nanoparticles Using Pluronic Block Copolymers[J]. 过程工程学报,2011,11.0(004):711. |
APA | 寿庆辉,郭晨,高红帅,周华从,刘春朝,&刘会洲.(2011).Facile Synthesis of Gold-nanoparticles-decorated Polymer Assemblies and Core-Shell Gold Nanoparticles Using Pluronic Block Copolymers.过程工程学报,11.0(004),711. |
MLA | 寿庆辉,et al."Facile Synthesis of Gold-nanoparticles-decorated Polymer Assemblies and Core-Shell Gold Nanoparticles Using Pluronic Block Copolymers".过程工程学报 11.0.004(2011):711. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论