Epoxy/α-alumina nanocomposite with high electrical insulation performance | |
Chen Yun1; Zhang Donghai1; Wu Xiaofeng1; Wang Haosheng1; Zhang Chong2; Yang Wei2; Chen Yunfa1 | |
刊名 | Progress in Natural Science: Materials International
![]() |
2017 | |
卷号 | 27期号:5页码:574 |
关键词 | Nanocomposite Epoxy resin insulation α-alumina |
ISSN号 | 1002-0071 |
英文摘要 | An experimental study was conducted to improve the electrical insulation of epoxy resin. The effects of boehmite, γ-alumina and α-alumina nanoparticles on the volume resistivity, dielectric strength and glass transition temperature of epoxy nanocomposites were investigated. The results showed that α-alumina nanoparticles displayed obvious advantages in enhancing electrical insulation performance of epoxy nanocomposites, compared to boehmite and γ-alumina nanoparticles. The direct current volume resistivity and breakdown strength of epoxy nanocomposite with 2.0 wt% α-alumina nanoparticles was improved to 2.2×10 18 Ω?cm and 76.1 kV·mm -1 respectively. And these improved values of electrical insulation properties are much higher than these of epoxy nanocomposites reported in previous studies. The main reason of these improvements may be that the epoxy |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.ipe.ac.cn/handle/122111/44932] ![]() |
专题 | 中国科学院过程工程研究所 |
作者单位 | 1.中国科学院过程工程研究所 2.Global Energy Interconnection Research Institute |
推荐引用方式 GB/T 7714 | Chen Yun,Zhang Donghai,Wu Xiaofeng,et al. Epoxy/α-alumina nanocomposite with high electrical insulation performance[J]. Progress in Natural Science: Materials International,2017,27(5):574. |
APA | Chen Yun.,Zhang Donghai.,Wu Xiaofeng.,Wang Haosheng.,Zhang Chong.,...&Chen Yunfa.(2017).Epoxy/α-alumina nanocomposite with high electrical insulation performance.Progress in Natural Science: Materials International,27(5),574. |
MLA | Chen Yun,et al."Epoxy/α-alumina nanocomposite with high electrical insulation performance".Progress in Natural Science: Materials International 27.5(2017):574. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论