Pebax?/TSIL blend thin film composite membranes for CO_2 separation

	Pebax?/TSIL blend thin film composite membranes for CO_2 separation
	Dai Zhongde 1; Bai Lu 2; Hval Karoline Navik 1; Zhang Xiangping 2; Zhang Suojiang 2; Deng Liyuan 1
刊名	Science China. Chemistry
	2016
卷号	59 期号:5 页码:538
关键词	CO_2 capture thin film composite membrane task specific ionic liquids Pebax post combustion
ISSN号	1674-7291
英文摘要	In this study a thin film composite (TFC) membrane with a Pebax/Task-specific ionic liquid (TSIL) blend selective layer was prepared. Defect-free Pebax/TSIL layers were coated successfully on a polysulfone ultrafiltration porous support with a polydimethylsiloxane (PDMS) gutter layer. Different parameters in the membrane preparation (e.g. concentration, coating time) were investigated and optimized. The morphology of the membranes was studied by scanning electron microscopy (SEM), while the thermal properties and chemical structures of the membrane materials were investigated by thermo-gravimetric analyzer (TGA), differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR). The CO_2 separation performance of the membrane was evaluated using a mixed gas permeation test. Experimental results show that the incorporation of TSIL into the Pebax matrix can significantly increase both CO_2 permeance and CO_2/N_2 selectivity. With the presence of water vapor, the membrane exhibits the best CO_2/N_2 selectivity at a relative humidity of around 75%, where a CO_2 permeance of around 500 GPU and a CO_2/N_2 selectivity of 46 were documented. A further increase in the relative humidity resulted in higher CO_2 permeance but decreased CO_2/N_2 selectivity. Experiments also show that CO_2 permeance decreases with a CO_2 partial pressure increase, which is considered a characteristic in facilitated transport membranes.
语种	英语
内容类型	期刊论文
源URL	[http://ir.ipe.ac.cn/handle/122111/44165]
专题	中国科学院过程工程研究所
作者单位	1.挪威科技大学 2.中国科学院过程工程研究所
推荐引用方式 GB/T 7714	Dai Zhongde,Bai Lu,Hval Karoline Navik,et al. Pebax?/TSIL blend thin film composite membranes for CO_2 separation[J]. Science China. Chemistry,2016,59(5):538.
APA	Dai Zhongde,Bai Lu,Hval Karoline Navik,Zhang Xiangping,Zhang Suojiang,&Deng Liyuan.(2016).Pebax?/TSIL blend thin film composite membranes for CO_2 separation.Science China. Chemistry,59(5),538.
MLA	Dai Zhongde,et al."Pebax?/TSIL blend thin film composite membranes for CO_2 separation".Science China. Chemistry 59.5(2016):538.