Effect of Surface Deposition Coating with Aluminum Hydroxide on the Stabilization of Iron-Arsenic Precipitates | |
Wang, Yongliang1; Liu, Xiang1,2; Yan, Jingmin1,2; Han, Peiwei1; Du, Yingchao1,2; Ye, Shufeng1 | |
刊名 | MINING METALLURGY & EXPLORATION
![]() |
2021-01-07 | |
页码 | 9 |
关键词 | Iron-arsenic coprecipitates Arsenic release Deposit Aluminum hydroxide Coating structure |
ISSN号 | 2524-3462 |
DOI | 10.1007/s42461-020-00366-8 |
英文摘要 | Iron-arsenic coprecipitate is a kind of solid waste produced in the treatment of arsenic-bearing wastewater from non-ferrous metallurgy. Stability of amorphous coprecipitates is usually poor if the Fe/As ratio is lower. In this study, the surface of coprecipitates was deposited with aluminum hydroxide with the aim to prevent the release of arsenic. The deposition experiments were carried out at normal temperature using Al-2(SO4)(3) solutions with pH between the range of 6.0-7.0. The characterization of the coated precipitates was investigated using SEM-EDS, TEM, XRD, FTIR, and BET. The stability experiment showed that the coated precipitates exhibit a higher release of arsenic than the coprecipitates without coating. The anion exchange might have taken place in the coated surface, and the release of arsenic may be a comprehensive result. |
资助项目 | Innovation Academy for Green Manufacture, Chinese Academy of Sciences[IAGM-2019-A05] ; Key Programs of the Chinese Academy of Sciences[ZDRW-ZS-2018-1] |
WOS关键词 | FERRIC ARSENATE ; ADSORBED ARSENATE ; COPRECIPITATION ; IMMOBILIZATION ; SCORODITE ; BEHAVIOR ; PH ; SOLIDIFICATION/STABILISATION ; NEUTRALIZATION ; REDUCTION |
WOS研究方向 | Metallurgy & Metallurgical Engineering ; Mining & Mineral Processing |
语种 | 英语 |
出版者 | SPRINGER HEIDELBERG |
WOS记录号 | WOS:000605934200003 |
资助机构 | Innovation Academy for Green Manufacture, Chinese Academy of Sciences ; Key Programs of the Chinese Academy of Sciences |
内容类型 | 期刊论文 |
源URL | [http://ir.ipe.ac.cn/handle/122111/43139] ![]() |
专题 | 中国科学院过程工程研究所 |
通讯作者 | Wang, Yongliang |
作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Sch Chem & Chem Engn, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Yongliang,Liu, Xiang,Yan, Jingmin,et al. Effect of Surface Deposition Coating with Aluminum Hydroxide on the Stabilization of Iron-Arsenic Precipitates[J]. MINING METALLURGY & EXPLORATION,2021:9. |
APA | Wang, Yongliang,Liu, Xiang,Yan, Jingmin,Han, Peiwei,Du, Yingchao,&Ye, Shufeng.(2021).Effect of Surface Deposition Coating with Aluminum Hydroxide on the Stabilization of Iron-Arsenic Precipitates.MINING METALLURGY & EXPLORATION,9. |
MLA | Wang, Yongliang,et al."Effect of Surface Deposition Coating with Aluminum Hydroxide on the Stabilization of Iron-Arsenic Precipitates".MINING METALLURGY & EXPLORATION (2021):9. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论