The Self-assembling and Application of Inorganic Antibacterial Material Made of Natural Nanoporous Carrier | |
Sun Chubao1; Zhou Beihai1; Ding Hao2; Zeng Dongdong3 | |
刊名 | JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION
![]() |
2008-12-01 | |
卷号 | 23期号:6页码:771-774 |
关键词 | inorganic antimicrobial nanoporous material antibacterial coating zeolite self-assembling |
ISSN号 | 1000-2413 |
其他题名 | J. Wuhan Univ. Technol.-Mat. Sci. Edit. |
中文摘要 | The inorganic anti microbial material was inhibited to the microbes with the added metal ion, Zn. The primary wet product carrying 5%-10% zinc ion was generated under the following conditions: temperature was 95 degrees C, solution zinc concentration was 1.2-2.0 mol/L, and the ratio of Zn solution to zeolite weight was 5 : 1. The final stable product was manufactured after baking in,in oven for 1-3 It at the temperature of 500-900 degrees C. The baked material was tested for its disinfection effectiveness and coloring effect when mixed with paint coating. Based on the final batch of tests, the zinc content Of this anti-microbial product was further optimized. |
英文摘要 | The inorganic anti microbial material was inhibited to the microbes with the added metal ion, Zn. The primary wet product carrying 5%-10% zinc ion was generated under the following conditions: temperature was 95 degrees C, solution zinc concentration was 1.2-2.0 mol/L, and the ratio of Zn solution to zeolite weight was 5 : 1. The final stable product was manufactured after baking in,in oven for 1-3 It at the temperature of 500-900 degrees C. The baked material was tested for its disinfection effectiveness and coloring effect when mixed with paint coating. Based on the final batch of tests, the zinc content Of this anti-microbial product was further optimized. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Materials Science, Multidisciplinary |
研究领域[WOS] | Materials Science |
关键词[WOS] | POWDERS ; ELECTROLYTE ; ZIRCONIA ; YSZ ; CONDUCTIVITY ; CATHODE ; SOFCS ; ZRO2 |
收录类别 | SCI |
原文出处 | |
语种 | 英语 |
WOS记录号 | WOS:000261845400001 |
公开日期 | 2013-10-08 |
内容类型 | 期刊论文 |
版本 | 出版稿 |
源URL | [http://ir.ipe.ac.cn/handle/122111/2846] ![]() |
专题 | 过程工程研究所_研究所(批量导入) |
作者单位 | 1.Univ Sci & Technol Beijing, Sch Civil & Environm Engn, Beijing 100083, Peoples R China 2.China Univ Geosci Beijing, Sch Mat Sci & Technol, Beijing 100083, Peoples R China 3.Chinese Acad Sci, Inst Proc Engn, Beijing 100080, Peoples R China |
推荐引用方式 GB/T 7714 | Sun Chubao,Zhou Beihai,Ding Hao,et al. The Self-assembling and Application of Inorganic Antibacterial Material Made of Natural Nanoporous Carrier[J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,2008,23(6):771-774. |
APA | Sun Chubao,Zhou Beihai,Ding Hao,&Zeng Dongdong.(2008).The Self-assembling and Application of Inorganic Antibacterial Material Made of Natural Nanoporous Carrier.JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,23(6),771-774. |
MLA | Sun Chubao,et al."The Self-assembling and Application of Inorganic Antibacterial Material Made of Natural Nanoporous Carrier".JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION 23.6(2008):771-774. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论