Effects of Heat Treatments on Microstructure and Mechanical Properties of AlSi10Mg Alloy Produced by Selective Laser Melting

doi:10.11900/0412.1961.2020.00253

CORC > 金属研究所 > 中国科学院金属研究所

	Effects of Heat Treatments on Microstructure and Mechanical Properties of AlSi10Mg Alloy Produced by Selective Laser Melting
	Wang Yue 1,2; Wang Jijie 2; Zhang Hao 1; Zhao Hongbo 1; Ni Dingrui 1; Xiao Bolv 1; Ma Zongyi 1
刊名	ACTA METALLURGICA SINICA
	2021-05-01
卷号	57 期号:5 页码:613-622
关键词	additive manufacturing selective laser melting AlSi10Mg alloy heat treatment mechanical property
ISSN号	0412-1961
DOI	10.11900/0412.1961.2020.00253
通讯作者	Ni Dingrui(drni@imr.ac.cn)
英文摘要	The urgent need for lightweight, high-accuracy, and personalized products has led to the rapid development of additive manufacturing. Selective laser melting (SLM), which is a very promising additive manufacturing technique, has attracted remarkable attention. The mechanical properties of SLM parts are highly related to the formation of pores and cracks. In this work, SLM parameters for AlSi10Mg alloy were optimized, and the SLM AlSi10Mg sample with a high relative density of 99.63% was obtained. The SLM sample exhibited good properties, including an ultimate tensile strength (UTS) of approximately 478 MPa, a total elongation of 8%, and an average hardness of 122 HV along the horizontal direction. However, due to a high cooling rate, an inhomogeneous microstructure with refined grains and a Si network was obtained. To achieve a homogeneous microstructure and further improve the elongation of the SLM samples, the effect of heat treatments on the microstructure and mechanical properties of the SLM samples along the horizontal direction was analyzed. After the heat treatments, the strength of the samples changed significantly and the elongation was significantly improved. Further, after a solid solution treatment at 540 degrees C for 1 h, the UTS significantly decreased to approximately 246 MPa and the elongation increased to more than 22%. For the sample annealed at 236 degrees C for 10 h, a UTS of approximately 368 MPa and elongation of approximately 17% were obtained. Moreover, the sample subjected to ageing at 130 degrees C for 4 h exhibited a high strength similar to the level of the SLM sample, the elongation was increased to approximately 11.9%, and the hardness was approximately 133 HV which is 10% higher than that of the SLM sample. The improved performance of the aged samples can be attributed to the combination of solution strengthening, microstructural refinement, and precipitation strengthening. The results show that low-temperature ageing is the optimized heat-treatment method for SLM samples with fine microstructures.
资助项目	National Key Research and Development Program of China[2017YFB0703104] ; Strategic Priority Research Program of the Chinese Academy of Sciences
WOS研究方向	Metallurgy & Metallurgical Engineering
语种	英语
出版者	SCIENCE PRESS
WOS记录号	WOS:000642002500005
资助机构	National Key Research and Development Program of China ; Strategic Priority Research Program of the Chinese Academy of Sciences
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/161255]
专题	金属研究所_中国科学院金属研究所
通讯作者	Ni Dingrui
作者单位	1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Shenyang Aerosp Univ, Coll Mat Sci & Engn, Shenyang 110136, Peoples R China
推荐引用方式 GB/T 7714	Wang Yue,Wang Jijie,Zhang Hao,et al. Effects of Heat Treatments on Microstructure and Mechanical Properties of AlSi10Mg Alloy Produced by Selective Laser Melting[J]. ACTA METALLURGICA SINICA,2021,57(5):613-622.
APA	Wang Yue.,Wang Jijie.,Zhang Hao.,Zhao Hongbo.,Ni Dingrui.,...&Ma Zongyi.(2021).Effects of Heat Treatments on Microstructure and Mechanical Properties of AlSi10Mg Alloy Produced by Selective Laser Melting.ACTA METALLURGICA SINICA,57(5),613-622.
MLA	Wang Yue,et al."Effects of Heat Treatments on Microstructure and Mechanical Properties of AlSi10Mg Alloy Produced by Selective Laser Melting".ACTA METALLURGICA SINICA 57.5(2021):613-622.