High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites | |
Kong, Xuan1; Liu, Yang2; Chen, Minghui1; Zhang, Tao1; Wang, Fuhui1 | |
刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS |
2021-02-09 | |
页码 | 13 |
关键词 | Oxidation Self-lubricating composites Wear Graphite |
ISSN号 | 1006-7191 |
DOI | 10.1007/s40195-020-01188-9 |
通讯作者 | Liu, Yang(liuyang@imr.ac.cn) ; Chen, Minghui(mhchen@mail.neu.edu.cn) |
英文摘要 | Nickel-graphite self-lubricating composites are a promising candidate to be used in turbine constructions that are usually exposed to high temperature oxidation and wear. However, the high-temperature stability of graphite as well as the effect that the oxide scale will play on the following wear process are still yet in debate. In this work, oxidation behavior of a NiCrAl-graphite composite and the subsequent friction and wear performances were studied. Results indicate that graphite is stable in the composites after oxidation at T <= 400 degrees C for 300 h, which contributes synergistically with the thin oxide film to self-lubrication. The friction coefficient is below 0.20 and the wear rate is similar to 1.43 x 10(-5) mm(3) N-1 m(-1). The composite has the highest friction coefficient and wear rate when it was suffered from the high temperature oxidation at 500 degrees C. Once it was oxidized at 600 degrees C, a glaze layer would develop during the subsequent sliding. It plays a positive role in improving tribological properties though in the absence of lubricant phase of graphite, with to be exactly the friction coefficient and wear rate reduced by 13% and 21%, respectively, in comparison with the case of oxidation at 500 degrees C. |
资助项目 | Fundamental Research Funds for the Central Universities[N180212008] ; Fundamental Research Funds for the Central Universities[N181003001] ; Ministry of Industry and Information Technology Project[MJ-2017-J-99] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
WOS记录号 | WOS:000616448400001 |
资助机构 | Fundamental Research Funds for the Central Universities ; Ministry of Industry and Information Technology Project |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/160589] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Liu, Yang; Chen, Minghui |
作者单位 | 1.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Kong, Xuan,Liu, Yang,Chen, Minghui,et al. High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2021:13. |
APA | Kong, Xuan,Liu, Yang,Chen, Minghui,Zhang, Tao,&Wang, Fuhui.(2021).High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites.ACTA METALLURGICA SINICA-ENGLISH LETTERS,13. |
MLA | Kong, Xuan,et al."High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites".ACTA METALLURGICA SINICA-ENGLISH LETTERS (2021):13. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论