Improving the oxidation behavior of low expansion Ni plus CrAlYNO coating systems by regulating the oxygen content | |
Jia, Yixuan1,3; Zhu, Shenglong3; Zhang, Kai1,3; Yang, Lanlan2; Liu, Zhengliang1,3; Shen, Mingli3; Wang, Fuhui4 | |
刊名 | CORROSION SCIENCE |
2021-08-15 | |
卷号 | 189页码:13 |
关键词 | A Metal matrix coating A Superalloys B TEM B Thermal cycling C Oxidation |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2021.109582 |
通讯作者 | Zhu, Shenglong(slzhu@imr.ac.cn) |
英文摘要 | The three duplex coatings comprised inner NiCrAlY layer and outer Ni + CrAlYNO cermet layer, which were referred to as N + 10O, N + 20O and N + 30O based on the oxygen content of flowing into the cermet layer, were prepared by a vacuum arc evaporation machine using a NiCrAlY target. Upon oxidation, the inclusion of YAG inside the alumina and the formation of non-alumina were detected in the N + 10O and N + 20O coatings. In comparison, the N + 30O coating through the slow growth rate and few impurities of TGO appeared superior oxidation resistance. This was mainly due to oxygen content on coatings degradation and Y distribution. |
资助项目 | National Key R&D Program of China[2018YFB2003601] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000677539100003 |
资助机构 | National Key R&D Program of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/159652] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhu, Shenglong |
作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 2.Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Jiangsu, Peoples R China 3.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 4.Northeastern Univ, Corros & Protect Div, Shengyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China |
推荐引用方式 GB/T 7714 | Jia, Yixuan,Zhu, Shenglong,Zhang, Kai,et al. Improving the oxidation behavior of low expansion Ni plus CrAlYNO coating systems by regulating the oxygen content[J]. CORROSION SCIENCE,2021,189:13. |
APA | Jia, Yixuan.,Zhu, Shenglong.,Zhang, Kai.,Yang, Lanlan.,Liu, Zhengliang.,...&Wang, Fuhui.(2021).Improving the oxidation behavior of low expansion Ni plus CrAlYNO coating systems by regulating the oxygen content.CORROSION SCIENCE,189,13. |
MLA | Jia, Yixuan,et al."Improving the oxidation behavior of low expansion Ni plus CrAlYNO coating systems by regulating the oxygen content".CORROSION SCIENCE 189(2021):13. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论