Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating

doi:10.1111/ijag.15513

CORC > 金属研究所 > 中国科学院金属研究所

	Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating
	Chen, Ken; Chen, Minghui; Yi, Aihua; Li, Kang; Zhu, Wen; Liao, Zhongmiao; Zhu, Shenglong; Wang, Fuhui
刊名	INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE
	2020-10-01
卷号	11 期号:4 页码:784-795
DOI	10.1111/ijag.15513
英文摘要	Dense and well-adherent enamel-nano-Ni composite/enamel-nano-nickel composite coatings were prepared on 304 steel. Their thermal shock (TS) resistance at 400 degrees C as well as the chemical stability in sulfuric acid solution were investigated, and compared with pure enamel coatings. Results indicated that the nanocomposite coatings with 5 wt% of Ni particles exhibited the best resistance to TS. Almost no spalling of the coating occurs after 50 cycles of TS at 400 degrees C. They also provided enough protective effect to the substrates from sulfuric acid corrosion. After 7 days of corrosion, the weight loss of Ni-5 enamel coating was only 1.107 mg/cm(.)(2)
WOS记录号	WOS:000530521500001
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/155702]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Chen, Ken,Chen, Minghui,Yi, Aihua,et al. Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating[J]. INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,2020,11(4):784-795.
APA	Chen, Ken.,Chen, Minghui.,Yi, Aihua.,Li, Kang.,Zhu, Wen.,...&Wang, Fuhui.(2020).Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating.INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,11(4),784-795.
MLA	Chen, Ken,et al."Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating".INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE 11.4(2020):784-795.