Effects of hot isostatic pressing and heat treatment process on microstructure and tensile properties of selective laser melting manufactured GH4169alloy

CORC > 金属研究所 > 中国科学院金属研究所

	Effects of hot isostatic pressing and heat treatment process on microstructure and tensile properties of selective laser melting manufactured GH4169alloy
	Shi Lei; Lei Liming; Wang Wei; Fu Xin; Zhang Guangping
刊名	Journal of Materials Engineering
	2020-07-12
卷号	48 期号:6 页码:148-155
英文摘要	GH4169alloys were manufactured by selective laser melting(SLM).The microstructure evolution and tensile properties of GH4169alloys during hot isostatic pressing(HIP)and heat treatment(HT)process were analyzed by OM,SEM,EBSD and TEM.The results show that the grains of the as-deposited samples in the building direction are columnar,exhibit very fine cellulardendritic structure with fine Laves phases precipitating in the interdendritic region.Most of porosities and Laves phases disappear after HIP,and the microstructure parallel to the building direction is transformed into equiaxed grains.Short rod-likedeltaphases are precipitated along grain boundaries after annealing at 980℃for 1h.The tensile properties at room temperature and 650℃of specimens after HIP and HT are higher than those of the standard requirements for the forgings,and the temperature has a little influence on the fracture mode.
WOS记录号	CSCD:6748769
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/155695]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Shi Lei,Lei Liming,Wang Wei,et al. Effects of hot isostatic pressing and heat treatment process on microstructure and tensile properties of selective laser melting manufactured GH4169alloy[J]. Journal of Materials Engineering,2020,48(6):148-155.
APA	Shi Lei,Lei Liming,Wang Wei,Fu Xin,&Zhang Guangping.(2020).Effects of hot isostatic pressing and heat treatment process on microstructure and tensile properties of selective laser melting manufactured GH4169alloy.Journal of Materials Engineering,48(6),148-155.
MLA	Shi Lei,et al."Effects of hot isostatic pressing and heat treatment process on microstructure and tensile properties of selective laser melting manufactured GH4169alloy".Journal of Materials Engineering 48.6(2020):148-155.