PRE-AGING OF RETROGRESSION AND RE-AGING OF SPRAY FORMED 7075 ALLOY

CORC > 金属研究所 > 中国科学院金属研究所

	PRE-AGING OF RETROGRESSION AND RE-AGING OF SPRAY FORMED 7075 ALLOY
	Su Ruiming; Qu Yingdong; Li Rongde
刊名	ACTA METALLURGICA SINICA
	2014
卷号	50 期号:7 页码:863-870
关键词	STRESS-CORROSION CRACKING GRAIN-BOUNDARY SEGREGATION STRENGTH ALUMINUM-ALLOYS PRECIPITATE-FREE ZONES AL-ALLOY MICROSTRUCTURE BEHAVIOR 7075 aluminum alloy spray forming retrogression and re-aging pre-aging precipitate
ISSN号	0412-1961
其他题名	PRE-AGING OF RETROGRESSION AND RE-AGING OF SPRAY FORMED 7075 ALLOY
英文摘要	Retrogression and re-aging (RRA) treatments are divided into pre-aging, retrogression and re-aging. Although peak aging was used as the pre-aging of RRA treatment in the past, some different opinions were reported in recent years. The effects of pre-aging of RBA treatment on microstructure, mechanical properties and conductivity of spray formed 7075 aluminum alloy were investigated by TEM, tensile and conductivity test. The results show that the mechanical properties and conductivity of spray formed 7075 alloy could be improved by the under aging at 120 degrees C for 16 h as the pre-aging of RRA treatment. The properties of the 7xxx series aluminum alloys depend on matrix precipitates (MPt), grain boundary precipitates (GBPs) and precipitate free zones (PFZs). The tiny MPt can increase the tensile strength. The connected GBPs and narrow PFZs will lower the conductivity and the elongation of the alloy. The under aging is more beneficial for the re-dissolution of the MPts at retrogression treatment at 200 degrees C for 10 min, and is more conducive to interrupt distributions of the GBPs than the early aging after RRA treatment. With the under aging as the pre-aging treatment, the growth of the MPts was actively suppressed and the GBPs at grain boundaries are continuous. During retrogression treatment, the MPts were re-dissolved absolutely and the GBPs were transformed from a chain to dissociation. After re-aging treatment, lots of tiny dispersive MPts precipitated out again in matrix, the GBPs were totally separated and the PFZ were widened. After pre-aging at 120 degrees C for 16 h and RRA treatment, the tensile strength and yield strength of the alloy are 782 and 726 MPa, respectively, which are higher than that after peak aging treatment or conventional RRA treatment, the conductivity of the 7075 alloy is excellent with 22.7 MS/m.
资助项目	[Fok Ying-Tong Education Foundation] ; [Program for Innovative Research Team in University of Liaoning Province]
语种	英语
CSCD记录号	CSCD:5188510
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/150158]
专题	金属研究所_中国科学院金属研究所
作者单位	中国科学院金属研究所
推荐引用方式 GB/T 7714	Su Ruiming,Qu Yingdong,Li Rongde. PRE-AGING OF RETROGRESSION AND RE-AGING OF SPRAY FORMED 7075 ALLOY[J]. ACTA METALLURGICA SINICA,2014,50(7):863-870.
APA	Su Ruiming,Qu Yingdong,&Li Rongde.(2014).PRE-AGING OF RETROGRESSION AND RE-AGING OF SPRAY FORMED 7075 ALLOY.ACTA METALLURGICA SINICA,50(7),863-870.
MLA	Su Ruiming,et al."PRE-AGING OF RETROGRESSION AND RE-AGING OF SPRAY FORMED 7075 ALLOY".ACTA METALLURGICA SINICA 50.7(2014):863-870.