Secondary Recrystallization of Nickel-Base Superalloy CM 247 LC After Processing by Metal Injection Molding | |
Sheng, Naicheng1,2; Meyer, Andreas1; Horke, Katharina4; Korner, Carolin1,3; Singer, Robert F.1,3 | |
刊名 | METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE |
2020-11-25 | |
页码 | 8 |
ISSN号 | 1073-5623 |
DOI | 10.1007/s11661-020-06087-3 |
通讯作者 | Sheng, Naicheng(ncsheng@imr.ac.cn) |
英文摘要 | Fabrication of parts by metal injection molding (MIM) results in very fine grain sizes. In the present investigation, heat treatments were employed to gain a larger grain size that is more creep resistant. The alloy under investigation was CM 247 LC. The composition was slightly modified to facilitate grain growth. Secondary recrystallization was observed to occur during post-sintering annealing treatments approximately 50 degrees C below the sintering temperature. The grain size increased from 25 mu m to > 2 mm. The increase of grain size was found to improve creep strength significantly. The samples in the as-sintered condition exhibited a bimodal grain size distribution. The grain size in a thin surface zone after sintering was slightly increased because of a lower C and O content in this zone that promoted normal grain growth. Secondary recrystallization did not occur in the surface zone. This is attributed to a lack of driving force in this area. |
资助项目 | Rolls-Royce Deutschland[20T1312A] ; Bundesministerium fur Wirtschaft und Energie BMWi (Federal Ministry for Economic Affairs and Energy)[20T1312A] ; Sieglinde Muller at Schunk Sintermetalltechnik GmbH |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SPRINGER |
WOS记录号 | WOS:000592566500001 |
资助机构 | Rolls-Royce Deutschland ; Bundesministerium fur Wirtschaft und Energie BMWi (Federal Ministry for Economic Affairs and Energy) ; Sieglinde Muller at Schunk Sintermetalltechnik GmbH |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/141451] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Sheng, Naicheng |
作者单位 | 1.Friedrich Alexander Univ Erlangen Nuremberg FAU, Joint Inst Adv Mat & Proc ZMP, Dr Mack Str 81, D-90762 Furth, Germany 2.Chinese Acad Sci, Inst Met Res, Shenyang, Peoples R China 3.Friedrich Alexander Univ Erlangen Nuremberg FAU, Dept Mat Sci, Inst Mat Sci & Engn Met WTM, Martensstr 5, D-91052 Erlangen, Germany 4.Rolls Royce Deutschland Ltd & Co KG, Eschenweg 11, D-15827 Dahlewitz, Blankenfelde Ma, Germany |
推荐引用方式 GB/T 7714 | Sheng, Naicheng,Meyer, Andreas,Horke, Katharina,et al. Secondary Recrystallization of Nickel-Base Superalloy CM 247 LC After Processing by Metal Injection Molding[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,2020:8. |
APA | Sheng, Naicheng,Meyer, Andreas,Horke, Katharina,Korner, Carolin,&Singer, Robert F..(2020).Secondary Recrystallization of Nickel-Base Superalloy CM 247 LC After Processing by Metal Injection Molding.METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,8. |
MLA | Sheng, Naicheng,et al."Secondary Recrystallization of Nickel-Base Superalloy CM 247 LC After Processing by Metal Injection Molding".METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE (2020):8. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论