Study on the Uniformity of Structure and Mechanical Properties of TC4-DT Alloy Deposited by CMT Process

doi:10.11900/0412.1961.2020.00104

CORC > 金属研究所 > 中国科学院金属研究所

	Study on the Uniformity of Structure and Mechanical Properties of TC4-DT Alloy Deposited by CMT Process
	Du Zijie 2,3; Li Wenyuan 3; Liu Jianrong 3; Suo Hongbo 1; Wang Qingjiang 3
刊名	ACTA METALLURGICA SINICA
	2020-12-11
卷号	56 期号:12 页码:1667-1680
关键词	CMT WAAM TC4-DT titanium alloy uniformity of microstructure texture uniformity of mechanical property
ISSN号	0412-1961
DOI	10.11900/0412.1961.2020.00104
通讯作者	Li Wenyuan(wyli@imr.ac.cn)
英文摘要	TC4-DT alloy is developed based on TC4 alloy, with medium strength and high damage-tolerance, showing a great promise to be widely used in aerospace field. However, the traditional method to fabricate large and complicated parts has the problems of hot working difficulty, long processing cycle, low "buy-to-fly" ratio and high-cost. Additive manufacturing (AM) technology is a good alternative and has been used to manufacture titanium parts since year 2006. Compared to other AM technologies, cold metal transfer mode wire and arc additive manufacturing (CMT WARM), as a kind of gas metal arc welding (GMAW) technology, has several advantages like simple structure, good spatial accessibility and high efficiency. In this study, a TC4-DT deposit was fabricated by CMT WAAM method. The macrostructure and microstructure, texture, and tensile properties in the overlapping zone and ordinary deposition zone were investigated and compared. The bottom of the ordinary deposition zone consisted of columnar and equiaxed prior beta grains, and in higher zone the coarse equiaxed prior beta grains were in the majority. The microstructure of the ordinary deposition zone was mainly characterized by basketweave alpha phase platelets. Microstructure of both sides of the overlapping line was characterized by a mixture of fine basketweave, lamellar and coarse basketweave a phase due to temperature gradient. Transformed alpha texture from {001}(beta)//Z silk texture existed in different zones, and the texture of overlapping zone was complicated due to the complexity of heat dissipation conditions, including transformed a texture and other complicated texture. EBSD results showed that there was a strong <0001>(alpha)//X texture at the overlapping line, resulting in low Schmid factors for both prismatic slip and basal slip at the overlapping line, hindering the slip of dislocation. Combined with the Hall-Petch relationship, it was concluded that the prior beta grain boundary and the overlapping line were main factors affecting the uniformity of mechanical properties. The average effective dislocation slip distances in different zones had the following relationship: overlapping zone.
WOS研究方向	Metallurgy & Metallurgical Engineering
语种	英语
出版者	SCIENCE PRESS
WOS记录号	WOS:000592474600009
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/141445]
专题	金属研究所_中国科学院金属研究所
通讯作者	Li Wenyuan
作者单位	1.Qingdao JointX Intelligent Mfg Ltd, Qingdao 266109, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Du Zijie,Li Wenyuan,Liu Jianrong,et al. Study on the Uniformity of Structure and Mechanical Properties of TC4-DT Alloy Deposited by CMT Process[J]. ACTA METALLURGICA SINICA,2020,56(12):1667-1680.
APA	Du Zijie,Li Wenyuan,Liu Jianrong,Suo Hongbo,&Wang Qingjiang.(2020).Study on the Uniformity of Structure and Mechanical Properties of TC4-DT Alloy Deposited by CMT Process.ACTA METALLURGICA SINICA,56(12),1667-1680.
MLA	Du Zijie,et al."Study on the Uniformity of Structure and Mechanical Properties of TC4-DT Alloy Deposited by CMT Process".ACTA METALLURGICA SINICA 56.12(2020):1667-1680.