Phase Characterization and Formation Behavior in 6 wt% Si High-silicon Austenitic Stainless Steel during Isothermal Aging | |
Chen, Sihan1,2; Liang, Tian1,3; Zhou, Yangtao1; Xing, Weiwei1; Zheng, Chengwu1; Ma, Yingche1; Wu, JinMing3; Li, Guobin4; Liu, Kui1 | |
刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS |
2020-10-14 | |
页码 | 8 |
关键词 | High-silicon austenitic stainless steel Precipitates chi-Phase Precipitation behavior |
ISSN号 | 1006-7191 |
DOI | 10.1007/s40195-020-01152-7 |
通讯作者 | Liang, Tian(tliang@imr.ac.cn) ; Liu, Kui(kliu@imr.ac.cn) |
英文摘要 | The precipitation behavior of different phases in a high-silicon stainless steel (6 wt% Si) during aging at 600-1050 degrees C for 24 h was investigated. The morphology, crystal structure and composition of various precipitates were detailly characterized using optical microscopy, scanning electron microscopy and transmission electron microscopy. Four phases were mainly identified:chi-phase,M6C carbides,sigma phase and a new type offcc-phase. During aging at 600-900 degrees C, the main precipitate was (Cr, Mo and Si)-rich chi-phase which was directly precipitated from gamma matrix. The chi-phase was calibrated as bcc structure with a lattice parameter of 8.90 A. The peak temperature for the precipitation of chi-phase was 800 degrees C, and it was dissolved when aging at temperatures above 1000 degrees C. The sigma-phase was observed only at 700 degrees C and grew next to chi-phase. Above 700 degrees C, a newfcc-phase was found to be precipitated along with chi-phase, with a space group ofFd3cand a lattice parameter of 12.56 A. TheM(6)C carbides started to be precipitated at 700 degrees C in the vicinity of chi-phase. And its amount basically increased with the increasing of temperature. An orientation relationship betweenM(6)C/gamma was found: [100]c//[100]gamma, (001)c//(001)gamma, i.e., the cube-on-cube relationship. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
WOS记录号 | WOS:000577229500001 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/140985] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Liang, Tian; Liu, Kui |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 3.Zhejiang Univ, Sch Mat Sci & Engn, State Key Lab Silicon Mat, Hangzhou 310027, Peoples R China 4.Zhejiang Xindeda Special Pipe Ind Co Ltd, Wenzhou 325024, Peoples R China |
推荐引用方式 GB/T 7714 | Chen, Sihan,Liang, Tian,Zhou, Yangtao,et al. Phase Characterization and Formation Behavior in 6 wt% Si High-silicon Austenitic Stainless Steel during Isothermal Aging[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2020:8. |
APA | Chen, Sihan.,Liang, Tian.,Zhou, Yangtao.,Xing, Weiwei.,Zheng, Chengwu.,...&Liu, Kui.(2020).Phase Characterization and Formation Behavior in 6 wt% Si High-silicon Austenitic Stainless Steel during Isothermal Aging.ACTA METALLURGICA SINICA-ENGLISH LETTERS,8. |
MLA | Chen, Sihan,et al."Phase Characterization and Formation Behavior in 6 wt% Si High-silicon Austenitic Stainless Steel during Isothermal Aging".ACTA METALLURGICA SINICA-ENGLISH LETTERS (2020):8. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论