Corrosion of phase and phase boundary in proton-irradiated 308L stainless steel weld metal in simulated PWR primary water

doi:10.1016/j.corsci.2019.108401

CORC > 金属研究所 > 中国科学院金属研究所

	Corrosion of phase and phase boundary in proton-irradiated 308L stainless steel weld metal in simulated PWR primary water
	Lin, Xiaodong 1,2; Peng, Qunjia 1,3; Mei, Jinna 3; Han, En-Hou 1; Ke, Wei 1; Qiao, Lijie 4; Jiao, Zhijie 5
刊名	CORROSION SCIENCE
	2020-04-01
卷号	165 页码:18
关键词	Stainless steel TEM Welding High temperature corrosion
ISSN号	0010-938X
DOI	10.1016/j.corsci.2019.108401
通讯作者	Peng, Qunjia(pengqunjia@yahoo.com)
英文摘要	The corrosion of austenite and delta-ferrite phases and the respective phase boundary was investigated in unirradiated and proton-irradiated 308 L stainless steel weld metal in a simulated-PWR environment. The results revealed that the inner oxide thickness was increased by irradiation for austenite but was largely unaffected for delta-ferrite. This behavior was attributed to the fact that irradiation generated numerous structure defects in austenite, but not in delta-ferrite. Following the 3-dpa (displacements per atom) irradiation, enhanced corrosion of delta-ferrite/austenite phase boundary occurred due to the irradiation-induced Cr-depletion. M23C6 carbides along the phase boundary further enhanced corrosion regardless of the irradiation condition.
资助项目	National Natural Science Foundation of China[51771031] ; National Natural Science Foundation of China[51571204] ; International Science & Technology Cooperation Program of China[2014DFA50800]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	PERGAMON-ELSEVIER SCIENCE LTD
WOS记录号	WOS:000518488800033
资助机构	National Natural Science Foundation of China ; International Science & Technology Cooperation Program of China
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/139003]
专题	金属研究所_中国科学院金属研究所
通讯作者	Peng, Qunjia
作者单位	1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Suzhou Nucl Power Res Inst, Suzhou 215004, Peoples R China 4.Univ Sci & Technol Beijing, Beijing Adv Innovat Ctr Mat Genet Engn, Beijing 100083, Peoples R China 5.Univ Michigan, Dept Nucl Engn & Radiol Sci, Ann Arbor, MI 48109 USA
推荐引用方式 GB/T 7714	Lin, Xiaodong,Peng, Qunjia,Mei, Jinna,et al. Corrosion of phase and phase boundary in proton-irradiated 308L stainless steel weld metal in simulated PWR primary water[J]. CORROSION SCIENCE,2020,165:18.
APA	Lin, Xiaodong.,Peng, Qunjia.,Mei, Jinna.,Han, En-Hou.,Ke, Wei.,...&Jiao, Zhijie.(2020).Corrosion of phase and phase boundary in proton-irradiated 308L stainless steel weld metal in simulated PWR primary water.CORROSION SCIENCE,165,18.
MLA	Lin, Xiaodong,et al."Corrosion of phase and phase boundary in proton-irradiated 308L stainless steel weld metal in simulated PWR primary water".CORROSION SCIENCE 165(2020):18.