High temperature tribological behaviors and wear mechanisms of NiAl-NbC-Ag composites formed by in-situ decomposition of AgNbO3 | |
Feng, Xiaochun2,3; Lu, Cheng2,3; Jia, Junhong1,2; Xue, Jiali1; Wang, Qihua2; Sun, Yuan4; Wang, Wenzhen2; Yi, Gewen2 | |
刊名 | TRIBOLOGY INTERNATIONAL |
2020 | |
卷号 | 141页码:9 |
关键词 | In-situ decomposition High temperature Tribological behaviors |
ISSN号 | 0301-679X |
DOI | 10.1016/j.triboint.2019.105898 |
通讯作者 | Jia, Junhong(jhjia@licp.cas.cn) ; Wang, Qihua(qhwang@licp.cas.cn) |
英文摘要 | NiAl-NbC-Ag composites were successfully prepared by vacuum-hot-pressing sintering with directly addition of AgNbO3 powders, where AgNbO3 were synthesized using a solid state reaction method. The tribological behaviors of composites were evaluated from 25 degrees C to 800 degrees C. The consequences reveal AgNbO3 are completely decomposed during sintering process and in-situ formed NiAl-NbC-Ag composites, which hold excellent high temperature tribologicial properties. At mid-low temperature, NAB20 (NiAl-20 wt%AgNbO3) has a relative lower friction coefficient compared to NiAl, which was attributed to the existence of Ag. While the lowered friction coefficients at 600 degrees C and 800 degrees C were attributed to the lubricating glaze layers formed by tribo-chemical reaction on the worn surfaces, which were consisted of typical layered structure Ag2Nb4O11, perovskite AgNbO3 with a highly flexible crystal structure and AgNb3O8. |
资助项目 | National Natural Science Foundation of China[51575505] ; National Natural Science Foundation of China[51675508] ; State Key Laboratory of Solid Lubrication[LSL-1610] |
WOS研究方向 | Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000505271400010 |
资助机构 | National Natural Science Foundation of China ; State Key Laboratory of Solid Lubrication |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/136483] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Jia, Junhong; Wang, Qihua |
作者单位 | 1.Shaanxi Univ Sci & Technol, Coll Mech & Elect Engn, Xian 710021, Shaanxi, Peoples R China 2.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China 3.Univ Chinese Acad Sci, Ctr Mat Sci & Optoelect Engn, Beijing 100049, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Dept Superalloys, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Feng, Xiaochun,Lu, Cheng,Jia, Junhong,et al. High temperature tribological behaviors and wear mechanisms of NiAl-NbC-Ag composites formed by in-situ decomposition of AgNbO3[J]. TRIBOLOGY INTERNATIONAL,2020,141:9. |
APA | Feng, Xiaochun.,Lu, Cheng.,Jia, Junhong.,Xue, Jiali.,Wang, Qihua.,...&Yi, Gewen.(2020).High temperature tribological behaviors and wear mechanisms of NiAl-NbC-Ag composites formed by in-situ decomposition of AgNbO3.TRIBOLOGY INTERNATIONAL,141,9. |
MLA | Feng, Xiaochun,et al."High temperature tribological behaviors and wear mechanisms of NiAl-NbC-Ag composites formed by in-situ decomposition of AgNbO3".TRIBOLOGY INTERNATIONAL 141(2020):9. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论