Dynamic recrystallization behavior of GH4169G alloy during hot compressive deformation | |
Jia, Dan1,2; Sun, Wenru1; Xu, Dongsheng1; Liu, Fang1 | |
刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY |
2019-09-01 | |
卷号 | 35期号:9页码:1851-1859 |
关键词 | GH4169G alloy Dynamic recrystallization Nucleation mechanism |
ISSN号 | 1005-0302 |
DOI | 10.1016/j.jmst.2019.04.018 |
通讯作者 | Sun, Wenru(wrsun@imr.ac.cn) |
英文摘要 | The microstructure evolutions and nucleation mechanisms of GH4169G alloy were studied by optical microscope, electron backscatter diffraction (EBSD) and transmission electron microscope (TEM). The hot compression tests were performed different imposed reductions in the range of true strain from 0.12 to 1.2 at the temperatures of 930 degrees-1050 degrees with strain rates of 0.01 s(-1)-1 s(-1). It is found that cumulative and local misorientation increase firstly and then decrease when the strain is increased due to the progress of dynamic recrystallization (DRX). The low angle boundaries (LAGBs) rapidly develop to high angle boundaries (HAGBs) at relatively high deformation temperature or the low strain rate. There are three DRX mechanisms observed for GH4169 G alloy during hot deformation. Discontinuous dynamic recrystallization (DDRX) as the dominant mechanism for GH4169 G alloy is characterized by typical necklace structures and bulged-original boundaries. Besides, different deformation bands with dislocation cells formed in deformed matrix at low temperature and large strain, which indicates that continuous dynamic recrystallization (CDRX) contributed to the DRX process. The twin boundaries lost their coherent characteristics and provide sites for nucleation, which also accelerates the nucleation of DRX. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | JOURNAL MATER SCI TECHNOL |
WOS记录号 | WOS:000475870600006 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/134714] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Sun, Wenru |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Jia, Dan,Sun, Wenru,Xu, Dongsheng,et al. Dynamic recrystallization behavior of GH4169G alloy during hot compressive deformation[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(9):1851-1859. |
APA | Jia, Dan,Sun, Wenru,Xu, Dongsheng,&Liu, Fang.(2019).Dynamic recrystallization behavior of GH4169G alloy during hot compressive deformation.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(9),1851-1859. |
MLA | Jia, Dan,et al."Dynamic recrystallization behavior of GH4169G alloy during hot compressive deformation".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.9(2019):1851-1859. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论