Localized Liquation and Resultant Pitting Corrosion Behavior of Welding Coarse-Grained Heat-Affected Zone in Niobium-Stabilized Austenitic Stainless Steel | |
Bai, Guanshun1,2; Li, Yiyi2; Lu, Shanping2 | |
刊名 | JOURNAL OF THE ELECTROCHEMICAL SOCIETY
![]() |
2018-08-09 | |
卷号 | 165期号:11页码:C722-C731 |
ISSN号 | 0013-4651 |
DOI | 10.1149/2.0091811jes |
通讯作者 | Lu, Shanping(shplu@inv.ac.cu) |
英文摘要 | Effect of localized liquation on pitting corrosion behavior of Nb-stabilized austenitic stainless steels was investigated by potentio-dynamic and potentiostatic polarization tests on the welding coarse-grained heat-affected zone (CGHAZ) samples simulated using finite-element software SYSWELD and Gleeble simulator. Results indicated that localized liquation gave rise to Nb-rich liquation bands along grain boundary, inhibiting metastable pit initiation and growth, but resulted in liquation cracks that facilitated the occurrence of stable pitting. Moreover, the large scatter in pitting potential and passive current density observed in CGHAZ samples was attributed to the heterogeneities in the distribution, geometry and dimensions of liquation cracks. (c) 2018 Ihe Electrochemical Society. |
资助项目 | National High Technology Research and Development Program of China[2012AA03A501] ; Research Program of Shenyang National Laboratory for Materials Science[2016RP020] |
WOS研究方向 | Electrochemistry ; Materials Science |
语种 | 英语 |
出版者 | ELECTROCHEMICAL SOC INC |
WOS记录号 | WOS:000441163300001 |
资助机构 | National High Technology Research and Development Program of China ; Research Program of Shenyang National Laboratory for Materials Science |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/128907] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Lu, Shanping |
作者单位 | 1.Ordnance Sci Inst China, Ningbo Branch, Ningbo 315103, Zhejiang, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Bai, Guanshun,Li, Yiyi,Lu, Shanping. Localized Liquation and Resultant Pitting Corrosion Behavior of Welding Coarse-Grained Heat-Affected Zone in Niobium-Stabilized Austenitic Stainless Steel[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY,2018,165(11):C722-C731. |
APA | Bai, Guanshun,Li, Yiyi,&Lu, Shanping.(2018).Localized Liquation and Resultant Pitting Corrosion Behavior of Welding Coarse-Grained Heat-Affected Zone in Niobium-Stabilized Austenitic Stainless Steel.JOURNAL OF THE ELECTROCHEMICAL SOCIETY,165(11),C722-C731. |
MLA | Bai, Guanshun,et al."Localized Liquation and Resultant Pitting Corrosion Behavior of Welding Coarse-Grained Heat-Affected Zone in Niobium-Stabilized Austenitic Stainless Steel".JOURNAL OF THE ELECTROCHEMICAL SOCIETY 165.11(2018):C722-C731. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论