Realising equal strength welding to parent metal in precipitation-hardened Al-Mg-Si alloy via low heat input friction stir welding | |
Zeng, X. H.1,2; Xue, P.1; Wang, D.1; Ni, D. R.1; Xiao, B. L.1; Ma, Z. Y.1 | |
刊名 | SCIENCE AND TECHNOLOGY OF WELDING AND JOINING
![]() |
2018 | |
卷号 | 23期号:6页码:478-486 |
关键词 | Precipitation-hardened Al alloy friction stir welding nanostructured grains strength |
ISSN号 | 1362-1718 |
DOI | 10.1080/13621718.2017.1415249 |
通讯作者 | Xue, P.(pxue@imr.ac.cn) ; Ma, Z. Y.(zyma@imr.ac.cn) |
英文摘要 | Two millimetres thick Al-Mg-Si (6061Al-T6) alloy plates were friction stir welded at various welding conditions. Under a low rotation rate of 400 rev min(-1) with rapid water cooling, the softening zone in the joint disappeared and a nanostructure with an average grain size of 80 nm was obtained in the stir zone (SZ). Therefore, a weld with equal strength to the parent metal (PM) was successfully achieved with the fracture occurring in the PM. Further, the average microhard-ness and ultimate tensile strength (UTS) of the SZs increased with the decreasing rotation rate and increasing cooling speed. The average microhardness and UTS of the SZ with nanostructure reached up to 134 HV and 505 MPa, respectively; though the initial strengthened precipitates disappeared. This work provides an effective strategy of achieving high property joints and enhancing the mechanical properties of precipitation-hardened Al alloys. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | TAYLOR & FRANCIS LTD |
WOS记录号 | WOS:000434196400004 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/128081] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Xue, P.; Ma, Z. Y. |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 2.Univ Chinese Acad Sci, Beijing, Peoples R China |
推荐引用方式 GB/T 7714 | Zeng, X. H.,Xue, P.,Wang, D.,et al. Realising equal strength welding to parent metal in precipitation-hardened Al-Mg-Si alloy via low heat input friction stir welding[J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING,2018,23(6):478-486. |
APA | Zeng, X. H.,Xue, P.,Wang, D.,Ni, D. R.,Xiao, B. L.,&Ma, Z. Y..(2018).Realising equal strength welding to parent metal in precipitation-hardened Al-Mg-Si alloy via low heat input friction stir welding.SCIENCE AND TECHNOLOGY OF WELDING AND JOINING,23(6),478-486. |
MLA | Zeng, X. H.,et al."Realising equal strength welding to parent metal in precipitation-hardened Al-Mg-Si alloy via low heat input friction stir welding".SCIENCE AND TECHNOLOGY OF WELDING AND JOINING 23.6(2018):478-486. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论