Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy | |
Huang, XB; Zhang, Y; Liu, YL; Hu, ZQ | |
刊名 | METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE |
1997-10-01 | |
卷号 | 28期号:10页码:2143-2147 |
ISSN号 | 1073-5623 |
通讯作者 | Huang, XB() |
英文摘要 | The shape, size, and content of MC carbides in a unidirectional Ni-base superalloy have been studied at different solidification rates using material of normal commercial composition (5 ppm nitrogen) and two melts with additions to produce 22 and 30 ppm nitrogen. M(C,N) was found in nitrogen-doped specimens. The increased nitrogen content results in a change in carbide morphology from acicular or Chinese-script type to a blocky one. Carbide size increases from 6.85 to 7.25 mu m at 2.5 mu m/s and from 2.31 to 2.81 mu m at 200 mu m/s as the nitrogen content increases from 5 to 22 ppm; carbide size is reduced to 5.2 mu m at 2.5 mu m/s and to 2.1 mu m at 200 mu m/s when nitrogen content is further raised to 30 ppm. There is no evident change in carbide content (area percentage) with increase of nitrogen. Scanning electron microscopy (SEM) and electron probe microanalysis revealed characteristic centers in some of the blocky carbides of TiN, as nuclei of MC or M(C,N) formed in the melt. The influences of nitrogen on carbide at the low solidification rate are stronger than those at the higher rate. With the increase of solidification rate, the carbide turns from bar to Chinese-script type, except for the base alloy at 2.5 mu m/s, and the content and size decrease. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | MINERALS METALS MATERIALS SOC |
WOS记录号 | WOS:A1997YA65600020 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/126808] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Huang, XB |
作者单位 | CHINESE ACAD SCI,MET RES INST,SHENYANG 110015,PEOPLES R CHINA |
推荐引用方式 GB/T 7714 | Huang, XB,Zhang, Y,Liu, YL,et al. Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,1997,28(10):2143-2147. |
APA | Huang, XB,Zhang, Y,Liu, YL,&Hu, ZQ.(1997).Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy.METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE,28(10),2143-2147. |
MLA | Huang, XB,et al."Effect of small amount of nitrogen on carbide characteristics in unidirectional Ni-base superalloy".METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE 28.10(1997):2143-2147. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论