Effect of Annealing Temperature on Hydrogen Storage Properties of LaNi3.8Al1.0Mn0.2 Alloy | |
Han Xingbo1,2; Yang Xiaojun3; Wang Pei3; Chen Wei1,2; Lin Zifeng1,2; Liu Guoliang1,2; Chen Demin1; Yang Ke1 | |
刊名 | RARE METAL MATERIALS AND ENGINEERING
![]() |
2016-04-01 | |
卷号 | 45期号:4页码:820-827 |
关键词 | hydrogen storage alloy annealing metal hydride |
ISSN号 | 1002-185X |
通讯作者 | Chen Demin(demin.chen.1@imr.ac.cn) |
英文摘要 | The LaNi3.8Al1.0Mn0.2 hydrogen storage alloy annealed at different temperatures (T=1173, 1223, 1273, 1323 K) was investigated to examine the effect of annealing temperature on the crystal structure, the activation and the hydrogen absorption/desorption performance. It is found that the non-CaCu5 phases becomes tinier and more dispersive after annealing. All the alloys consist of the same matrix phase with CaCu5 type structure. Although it is more difficult to activate the annealed alloy than the as-cast alloy, the activation becomes easier with the increase of annealing temperature for the annealed alloy. The plateau pressure decreases at first with the increase of annealing temperature, when T <= 1223 K and then increases. Changes in both the lattice strain and the pressure plateau slope factor of Sf in the alloys show the same trends with that of the annealing temperature, exhibiting a maximum at T=1223 K. It is also found that the absolute value of the enthalpy increases with the increase of annealing temperature, when T <= 1223 K and then decreases, showing the same change trend as that of the cell volume. Moreover, the pulverization resistance and kinetics of the alloy are improved by annealing. The pulverization resistance is weakened at first with the increase of annealing temperature when T <= 1223 K and then increases, but the kinetics of the alloy is almost not influenced by the annealing temperature. |
资助项目 | National Natural Science Foundation of China[51271176] ; National Basic Research Program of China[2010CB631305] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000375490600001 |
资助机构 | National Natural Science Foundation of China ; National Basic Research Program of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/122147] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Chen Demin |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.China Natl Nucl Corp, Ltd 404, Lanzhou 732850, Peoples R China |
推荐引用方式 GB/T 7714 | Han Xingbo,Yang Xiaojun,Wang Pei,et al. Effect of Annealing Temperature on Hydrogen Storage Properties of LaNi3.8Al1.0Mn0.2 Alloy[J]. RARE METAL MATERIALS AND ENGINEERING,2016,45(4):820-827. |
APA | Han Xingbo.,Yang Xiaojun.,Wang Pei.,Chen Wei.,Lin Zifeng.,...&Yang Ke.(2016).Effect of Annealing Temperature on Hydrogen Storage Properties of LaNi3.8Al1.0Mn0.2 Alloy.RARE METAL MATERIALS AND ENGINEERING,45(4),820-827. |
MLA | Han Xingbo,et al."Effect of Annealing Temperature on Hydrogen Storage Properties of LaNi3.8Al1.0Mn0.2 Alloy".RARE METAL MATERIALS AND ENGINEERING 45.4(2016):820-827. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论