HIGH-CYCLE FATIGUE BEHAVIOR OF K416B Ni-BASED CASTING SUPERALLOY AT 700 degrees C | |
Xie Jun; Yu Jinjiang; Sun Xiaofeng; Jin Tao | |
刊名 | ACTA METALLURGICA SINICA
![]() |
2016-03-11 | |
卷号 | 52期号:3页码:257-263 |
关键词 | K416B Ni-based superalloy high-cycle fatigue deformation mechanism fracture feature |
ISSN号 | 0412-1961 |
通讯作者 | Yu Jinjiang(jjyu@imr.ac.cn) |
英文摘要 | Ni-based speralloys have been widely used to make the blade parts of the advanced aeroengines for their high temperature tolerance and good mechanical property. During high temperature service, the materials endure the effects of temperature and alternating load, causing high-cycle fatigue deformation on the hot-end components. Meanwhile, the fatigue behaviors of the alloy are closely related to the deformation mechanisms and its microstructure characteristics, such as the size, distribution and morphology of gamma' phase and carbides, and the fatigue fracture of the using materials possesses unpredictability. Therefore, investigating fatigue behaviors of the material is of significance in alloy design and life prediction. But the high-cycle fatigue behavior of K416B superalloy with high W content is still unclear up to now. For this reason, by means of high-cycle fatigue property measurement and microstructure observation, the high-cycle fatigue behavior of K416B Ni-based superalloy at 700 degrees C has been investigated. The results show that at 700 degrees C and stress ratio R=-1, the high-cycle fatigue life of K416B super alloy decreases with the stress increasing, and high-cycle fatigue strength of the alloy is 175 MPa. At the condition of low stress amplitude, the deformed dislocations may slip along different orientations in the matrix. With the stress amplitude increasing, the dislocations may shear into gamma' phase and form the stacking fault. During tension and compression high-cycle fatigue, multiple slip systems are activated in the alloy, and the distortion occurs along various directions, resulting in stress concentration on the regions of gamma+gamma' eutectic and carbides. The crack sources may be initiated at the eutectic and blocky carbide near the surface of the alloy. As high-cycle fatigue goes on, the cracks propagate along the inter-dendrite in expansion 'region, and the typical cleavage fracture occurs in the final rupture region. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SCIENCE PRESS |
WOS记录号 | WOS:000372691500001 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/121832] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Yu Jinjiang |
作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Xie Jun,Yu Jinjiang,Sun Xiaofeng,et al. HIGH-CYCLE FATIGUE BEHAVIOR OF K416B Ni-BASED CASTING SUPERALLOY AT 700 degrees C[J]. ACTA METALLURGICA SINICA,2016,52(3):257-263. |
APA | Xie Jun,Yu Jinjiang,Sun Xiaofeng,&Jin Tao.(2016).HIGH-CYCLE FATIGUE BEHAVIOR OF K416B Ni-BASED CASTING SUPERALLOY AT 700 degrees C.ACTA METALLURGICA SINICA,52(3),257-263. |
MLA | Xie Jun,et al."HIGH-CYCLE FATIGUE BEHAVIOR OF K416B Ni-BASED CASTING SUPERALLOY AT 700 degrees C".ACTA METALLURGICA SINICA 52.3(2016):257-263. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论