PREPARATION AND MECHANICAL PROPERTIES OF Zr46.9Cu45.5Al5.6Y2.0 IN SITU BMG COMPOSITES WITH B2-CuZr PHASE | |
Shen Yong; Xu Jian | |
刊名 | ACTA METALLURGICA SINICA |
2015-11-01 | |
卷号 | 51期号:11页码:1407-1415 |
关键词 | bulk metallic glass composite B2-CuZr fracture toughness |
ISSN号 | 0412-1961 |
通讯作者 | Shen Yong(yongshen@imr.ac.cn) |
英文摘要 | Bulk metallic glass (BMG) composites containing B2-CuZr phase are of interest due to they behave large plastic strain and apparent work hardening in tension. Nevertheless till now most BMG composites containing B2-CuZr phase are based on Cu-47 Zr-5(47) Al-5(5) or Zr48Cu47 5Al4Co0.5 BMG, which has limited glass forming ability (GFA). The prepared sample size is small, which restricts their potential engineering structural applications. In this work, Zr-Cu-Al-Y quaternary system is selected due to its high GFA. By tuning composition close to CuZr alloy in Zr-Cu-Al-Y quaternary system, Zr46.9Cu45.5Al5.6Y2 0 BMG is selected because it has proper GFA (critical diameter D-c=5 mm) and relatively large fracture toughness (K-Q=(49 +/- 3) MPa.m(1/2)). By decreasing the cooling rates of the melt via increasing diameter of casting rods, large-sized in situ Zr-46 9Cu45.5Al5.6Y2.0 BMG composites containing 13% and 25% volume fractions spherical B2-CuZr phase were prepared in the casting rods with 6 and 7 mm in diameters, respectively. In compression testing, the in situ BMG composites containing 25%B2-CuZr phase promote multiple shear bands within glass matrix and remarkable global plastic deformation, accompanied by a large compressive plastic strain as 6.5%. Nevertheless in tension testing no obvious global ductility was achieved, which attributes to the low mode I fracture toughness and small plastic zone size (R-P=88 mu m, R-P=(1/3 pi)(K-Q/sigma(y))(2)) of glass matrix. Three point bending test results show that Y has an adverse effect on the fracture toughness and plastic zone size of Zr-Cu-Al BMGs. In contrast to Zr46.9Cu45 5Al5.6Y2 0 BMG, fatigue pre-cracked Zr48Cu45Al7 BMG plate samples can be prepared and exhibit a high fracture toughness (K-Q=(62 +/- 3) MPa.m(1/2)) and a large plastic zone size (R-P=150 mu m) in plane strain state. Our results show that GFA and fracture toughness of glass matrix should be balanced when designing new BMG composites containing B2-CuZr phase. |
资助项目 | National Natural Science Foundation of China[51171180] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SCIENCE PRESS |
WOS记录号 | WOS:000365456100014 |
资助机构 | National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/121257] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Shen Yong |
作者单位 | Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Shen Yong,Xu Jian. PREPARATION AND MECHANICAL PROPERTIES OF Zr46.9Cu45.5Al5.6Y2.0 IN SITU BMG COMPOSITES WITH B2-CuZr PHASE[J]. ACTA METALLURGICA SINICA,2015,51(11):1407-1415. |
APA | Shen Yong,&Xu Jian.(2015).PREPARATION AND MECHANICAL PROPERTIES OF Zr46.9Cu45.5Al5.6Y2.0 IN SITU BMG COMPOSITES WITH B2-CuZr PHASE.ACTA METALLURGICA SINICA,51(11),1407-1415. |
MLA | Shen Yong,et al."PREPARATION AND MECHANICAL PROPERTIES OF Zr46.9Cu45.5Al5.6Y2.0 IN SITU BMG COMPOSITES WITH B2-CuZr PHASE".ACTA METALLURGICA SINICA 51.11(2015):1407-1415. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论