Effects of environment on the overload behavior of fatigue | |
Guan, H; Li, J; Wei, XJ; Han, EH; Ke, W | |
刊名 | ACTA METALLURGICA SINICA
![]() |
2003-06-01 | |
卷号 | 39期号:6页码:613-616 |
关键词 | environment stainless steel fatigue crack propagation overload |
ISSN号 | 0412-1961 |
通讯作者 | Guan, H() |
英文摘要 | The effects of 3.5% NaCl aqueous solution on the overload retardation behaviour of AISI 321 stainless steel fatigued under constant DeltaK was investigated. The results show that, compared with the air, the environment reduces the overload retardation effect significantly, although the overload behaviors in the air and environment are similar. The reducing level is approximately 40%-70% in terms of loss cycle number, and 30-40% in terms of overload affecting zone size. The comparison of the above two parameters shows that the former is not a proper parameter to describe the overload effect because of not distinguishing between the strengthening and reducing effects of environment on the crack closure. The later is a better parameter to describe the overload effect because it can distinguish the environmental effect on the crack closure from the comprehensively environmental effects on both crack closure and crack tip. SEM analysis of the fracture surface shows that the overload plastic strain suffered more erosion in environment than in air. It is suggested that the reduction of the plasticity-induced crack closure caused by environmental corrosion-erosion is responsible for the reduction of the overload retardation effect. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SCIENCE CHINA PRESS |
WOS记录号 | WOS:000183958400012 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/117919] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Guan, H |
作者单位 | 1.Chinese Acad Sci, Met Res Inst, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China 2.Fudan Univ, Dept Mat Sci, Shanghai 200433, Peoples R China |
推荐引用方式 GB/T 7714 | Guan, H,Li, J,Wei, XJ,et al. Effects of environment on the overload behavior of fatigue[J]. ACTA METALLURGICA SINICA,2003,39(6):613-616. |
APA | Guan, H,Li, J,Wei, XJ,Han, EH,&Ke, W.(2003).Effects of environment on the overload behavior of fatigue.ACTA METALLURGICA SINICA,39(6),613-616. |
MLA | Guan, H,et al."Effects of environment on the overload behavior of fatigue".ACTA METALLURGICA SINICA 39.6(2003):613-616. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论