Crystallization of the amorphous alloy Fe-Mo-W-B obtained by electroless plating

CORC > 金属研究所 > 中国科学院金属研究所

	Crystallization of the amorphous alloy Fe-Mo-W-B obtained by electroless plating
	Wang, LL ; Zhao, LH ; Zhang, BW ; Hu, WY ; Shu, XL ; Ouyang, YF ; Liao, SZ
刊名	RARE METAL MATERIALS AND ENGINEERING
	1998-10-01
卷号	27 期号:5 页码:282-285
关键词	electroless plating Fe - Mo - W - B alloy crystallization
ISSN号	1002-185X
通讯作者	Wang, LL()
英文摘要	Amorphous Fe-Mo-W-B alloy deposits have been made by electroless plating. The structure and the crystallization of the alloy have been studied by X -ray diffraction (XRD). It is found that the structure is amorphous if the boron content is within the range of 9.8 at% to 27.3 at%, which is wider than that of the binary Fe - B, but narrower than that of ternary Fe - Mo - B amorphous film. A two -step crystallization process is observed for the deposits. At first, the crystalline phases alpha-Fe, Fe3B and (Mot W)(2)B precipitates, followed by amorphous Fe3B; (Mo,W)B and Fe-2(Mo,W) films form at high temperature.
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	NORTHWEST INST NONFERROUS METAL RESEARCH
WOS记录号	WOS:000076927500008
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/108334]
专题	金属研究所_中国科学院金属研究所
通讯作者	Wang, LL
作者单位	1.Hunan Univ, Dept Appl Phys, Changsha 410082, Peoples R China 2.Acad Sinica, Int Ctr Mat Phys, Shenyang 110015, Peoples R China 3.Guangxi Univ, Dept Phys, Nanning 530004, Peoples R China 4.Hunan Educ Inst, Dept Phys, Changsha 410012, Peoples R China
推荐引用方式 GB/T 7714	Wang, LL,Zhao, LH,Zhang, BW,et al. Crystallization of the amorphous alloy Fe-Mo-W-B obtained by electroless plating[J]. RARE METAL MATERIALS AND ENGINEERING,1998,27(5):282-285.
APA	Wang, LL.,Zhao, LH.,Zhang, BW.,Hu, WY.,Shu, XL.,...&Liao, SZ.(1998).Crystallization of the amorphous alloy Fe-Mo-W-B obtained by electroless plating.RARE METAL MATERIALS AND ENGINEERING,27(5),282-285.
MLA	Wang, LL,et al."Crystallization of the amorphous alloy Fe-Mo-W-B obtained by electroless plating".RARE METAL MATERIALS AND ENGINEERING 27.5(1998):282-285.