Ultra-high cycle fatigue behavior of Ti-6Al-4V alloy | |
Zuo Jinghui; Wang Zhongguang; Han Enhou | |
刊名 | ACTA METALLURGICA SINICA
![]() |
2007-07-01 | |
卷号 | 43期号:7页码:705-709 |
关键词 | ultra-high cycle fatigue fatigue strength fatigue limit bimodal microstructure basketweave microstruture |
ISSN号 | 0412-1961 |
通讯作者 | Han Enhou(ehhan@imr.ac.cn) |
英文摘要 | The fatigue S-N curves of Ti-6Al-4V alloys with the bimodal and basketweave microstructures were determined between 10(5)-10(9) cyc using the ultrasonic fatigue testing system under a loading frequency of 20 kHz. The fracture surfaces of specimens were investigated with SEM. The results show that the S-N curves of Ti-6Al-4V with two kinds of microstructures continue to decrease with increasing the number of cycles and have no horizontal asymptote in the regime of 10(5)-10(9) cyc, so no conventional fatigue limits exist for Ti-6Al-4V with the two microstructures. SEM analysis shows that the crack initiation sites change from the surface to interior of specimens with decreasing the load amplitude, and therefore formed a bimodal failure distribution. The fatigue lifetime is higher under the frequency of 20 kHz as compared with that under the frequency of 25 Hz. Especially, the fatigue behavior of the basketweave microstructure shows more pronounced frequency effect than that of bimodal microstructure. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SCIENCE CHINA PRESS |
WOS记录号 | WOS:000248548200007 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/91531] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Han Enhou |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Environm Corros Ctr, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Zuo Jinghui,Wang Zhongguang,Han Enhou. Ultra-high cycle fatigue behavior of Ti-6Al-4V alloy[J]. ACTA METALLURGICA SINICA,2007,43(7):705-709. |
APA | Zuo Jinghui,Wang Zhongguang,&Han Enhou.(2007).Ultra-high cycle fatigue behavior of Ti-6Al-4V alloy.ACTA METALLURGICA SINICA,43(7),705-709. |
MLA | Zuo Jinghui,et al."Ultra-high cycle fatigue behavior of Ti-6Al-4V alloy".ACTA METALLURGICA SINICA 43.7(2007):705-709. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论