Rust Conversion Performance of Phosphoric Acid-Gallic Acid in Vinyl Chloride Acrylic Emulsion | |
Wang, Xin1,2,3,4; Zhu, Qingjun1,2,3,4; Liu, Xiangju1,2,3; Hou, Baorong1,2,3,4 | |
刊名 | COATINGS |
2021-02-01 | |
卷号 | 11期号:2页码:14 |
关键词 | rust conversion coating anticorrosion gallic acid acrylic emulsion rust converter |
DOI | 10.3390/coatings11020152 |
通讯作者 | Zhu, Qingjun(zhuqingjun@qdio.ac.cn) ; Hou, Baorong(baoronghou@163.com) |
英文摘要 | This work studied the application of phosphoric acid-gallic acid in vinyl chloride acrylic emulsion and its rust conversion performance. The increase of phosphoric acid affected the stability of the system, leading to the rapid precipitation of flocculent precipitation. Rust conversion coating (RCC) showed the best synergistic conversion effect when gallic acid (GA) was 0.2 wt.% and phosphoric acid (PA) was 2 wt.%. XRD and FTIR analysis show that the components of adherent rust (AR) are alpha-FeOOH, gamma-FeOOH and Fe3O4. The conversion products are ferric phosphate (FP) and ferric gallate (FG). The RCC can effectively treat the rusted steel (RS) produced by simulated marine atmospheric corrosion. The corrosion current density was reduced by three orders of magnitude, the adhesion reached 2.75 MPa, and the salt spray corrosion resistance was 20 days. The results of Raman, XPS, SEM and EDS show that the ionic dissolution of iron, complexation and further oxidation reactions occur at the interface between the adherent rust and the RCC. After rust conversion treatment, unreacted rust (UR) affects the further improvement of adhesion strength and anti-corrosion performance. |
资助项目 | National Natural Science Foundation of China[41827805] ; Shandong Provincial Natural Science Foundation[ZR2020MD080] |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000622364600001 |
内容类型 | 期刊论文 |
源URL | [http://ir.qdio.ac.cn/handle/337002/169594] |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
通讯作者 | Zhu, Qingjun; Hou, Baorong |
作者单位 | 1.Chinese Acad Sci, Inst Oceanol, CAS Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China 2.Chinese Acad Sci, Ctr Ocean Mega Sci, 7 Nanhai Rd, Qingdao 266071, Peoples R China 3.Pilot Natl Lab Marine Sci & Technol Qingdao, Open Studio Marine Corros & Protect, Qingdao 266237, Peoples R China 4.Univ Chinese Acad Sci, Coll Earth & Planetary Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Xin,Zhu, Qingjun,Liu, Xiangju,et al. Rust Conversion Performance of Phosphoric Acid-Gallic Acid in Vinyl Chloride Acrylic Emulsion[J]. COATINGS,2021,11(2):14. |
APA | Wang, Xin,Zhu, Qingjun,Liu, Xiangju,&Hou, Baorong.(2021).Rust Conversion Performance of Phosphoric Acid-Gallic Acid in Vinyl Chloride Acrylic Emulsion.COATINGS,11(2),14. |
MLA | Wang, Xin,et al."Rust Conversion Performance of Phosphoric Acid-Gallic Acid in Vinyl Chloride Acrylic Emulsion".COATINGS 11.2(2021):14. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论