mechanicalpropertiesandfrictionbehaviorsofcntalsi10mgcompositesproducedbysparkplasmasintering | |
Wang Linzhi3; Liu Ying2; Wu Jiaojiao3; Zhang Xi1 | |
刊名 | 矿物冶金与材料学报 |
2017 | |
卷号 | No.5期号:5页码:584 |
ISSN号 | 1674-4799 |
英文摘要 | The mechanical properties and friction behaviors of CNT/AlSi_(10)Mg composites produced by spark plasma sintering (SPS) were investigated. The results showed that the densities of the sintered composites gradually increased with increasing sintering temperature and that the highest microhardness and compressive strength were achieved in the specimen sintered at 450°C. CNTs dispersed uniformly in the Al- Si_(10)Mg matrix when the addition of CNTs was less than 1.5wt%. However, when the addition of CNTs exceeded 1.5wt%, the aggregation of CNTs was clearly observed. Moreover, the mechanical properties (including the densities, compressive strength, and microhardness) of the composites changed with CNT content and reached a maximum value when the CNT content was 1.5wt%. Meanwhile, the minimum average friction coefficient and wear rate of the CNT/AlSi_(10)Mg composites were obtained with 1.0wt% CNTs. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.138/handle/2HOD01W0/9137] |
专题 | 中国科学院重庆绿色智能技术研究院 |
作者单位 | 1.西南交通大学 2.四川大学 3.中国科学院重庆绿色智能技术研究院 |
推荐引用方式 GB/T 7714 | Wang Linzhi,Liu Ying,Wu Jiaojiao,et al. mechanicalpropertiesandfrictionbehaviorsofcntalsi10mgcompositesproducedbysparkplasmasintering[J]. 矿物冶金与材料学报,2017,No.5(5):584. |
APA | Wang Linzhi,Liu Ying,Wu Jiaojiao,&Zhang Xi.(2017).mechanicalpropertiesandfrictionbehaviorsofcntalsi10mgcompositesproducedbysparkplasmasintering.矿物冶金与材料学报,No.5(5),584. |
MLA | Wang Linzhi,et al."mechanicalpropertiesandfrictionbehaviorsofcntalsi10mgcompositesproducedbysparkplasmasintering".矿物冶金与材料学报 No.5.5(2017):584. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论