Crystal structure, phase evolution and dielectric properties in the Li2ZnTi3O8-SrTiO3 system as temperature stable high-Q material

doi:10.1016/j.jallcom.2019.05.084

	Crystal structure, phase evolution and dielectric properties in the Li2ZnTi3O8-SrTiO3 system as temperature stable high-Q material
	Ren, Haishen; Xie, Tianyi; Wu, Zhilun; He, Fei; Zhang, Yi; Jiang, Shaohu; Yao, Xiaogang; Lin, Huixing
刊名	JOURNAL OF ALLOYS AND COMPOUNDS
	2019-08-15
卷号	797 页码:18
关键词	Li2ZnTi3O8-SrTiO3 composite ceramic Temperature stable material Crystal structure Dielectric properties
ISSN号	0925-8388
DOI	10.1016/j.jallcom.2019.05.084
文献子类	Article
英文摘要	In this paper, the crystal structure, phase evolution, microstructure and microwave dielectric properties were investigated in Li2Zn(1-x)Ti3O8-xSrTiO(3) (x = 0-0.075) ceramic system well-sintered at 1075 degrees C for 4 h through one-step solid state reaction route. The XRD results showed that except for the main Li(2)Z-nTi(3)O(8) phase, the unknown phase started appearing at x = 0.01, and as x value was further increased to 0.025, the SrTiO3 phase appeared in sample and the relative content gradually increased. However, the slight deficiency of Zn2+ (x <= 0.025) could be used the decrease of molecular volume for Li2ZnTi3O8 crystal structure. Consequently, the relative permittivity (epsilon(r)) and temperature coefficient of resonant frequency (tau(f)) demonstrated a trend of fall first then rise as the cutoff point in x = 0.01, whereas the quality factor (Q x f) increased initially and then decreased. Typically, the Li2Zn0.95Ti3O8-0.05SrTiO(3) ceramic showed a temperature stable high-Q material with epsilon(r) = 26.6, Q x f = 62300 GHz, and tau(f) = 0.27 ppm/degrees C. It could be found that the variation of Li2ZnTi3O8 crystal structure had an essential effect on dielectric properties of composite with <= 0.01, whereas that of composite with x >= 0.025 was determined by the relative content of Li2ZnTi3O8 and SrTiO3 phase. In addition, the unknown phase seemed to have no effect on dielectric properties. (C) 2019 Elsevier B.V. All rights reserved.
WOS研究方向	Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	ELSEVIER SCIENCE SA
内容类型	期刊论文
源URL	[http://ir.sic.ac.cn/handle/331005/26907]
专题	中国科学院上海硅酸盐研究所
推荐引用方式 GB/T 7714	Ren, Haishen,Xie, Tianyi,Wu, Zhilun,et al. Crystal structure, phase evolution and dielectric properties in the Li2ZnTi3O8-SrTiO3 system as temperature stable high-Q material[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2019,797:18.
APA	Ren, Haishen.,Xie, Tianyi.,Wu, Zhilun.,He, Fei.,Zhang, Yi.,...&Lin, Huixing.(2019).Crystal structure, phase evolution and dielectric properties in the Li2ZnTi3O8-SrTiO3 system as temperature stable high-Q material.JOURNAL OF ALLOYS AND COMPOUNDS,797,18.
MLA	Ren, Haishen,et al."Crystal structure, phase evolution and dielectric properties in the Li2ZnTi3O8-SrTiO3 system as temperature stable high-Q material".JOURNAL OF ALLOYS AND COMPOUNDS 797(2019):18.