Degradation of the oxide film formed on Alloy 690TT in a high-temperature chloride solution

	Degradation of the oxide film formed on Alloy 690TT in a high-temperature chloride solution
	Hou Qiang ; Liu Zhiyong ; Li Chengtao ; Li Xiaogang ; Shao Jiamin
刊名	APPLIED SURFACE SCIENCE
	2019
卷号	467 页码:1104-1112
关键词	STRESS-CORROSION CRACKING AUSTENITIC STAINLESS-STEEL NI-BASED ALLOYS SUPERCRITICAL WATER PASSIVE FILMS OXIDATION BEHAVIOR SULFATE LEAD THIOSULFATE INITIATION
DOI	10.1016/j.apsusc.2018.10.196
英文摘要	Degradation of the oxide film formed on Alloy 690TT in a high-temperature chloride solution
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/18557]
专题	2019专题
作者单位	1.Liu, ZY 2.Li, XG (reprint author), Univ Sci & Technol Beijing, Corros & Protect Ctr, Beijing 100083, Peoples R China.
推荐引用方式 GB/T 7714	Hou Qiang,Liu Zhiyong,Li Chengtao,et al. Degradation of the oxide film formed on Alloy 690TT in a high-temperature chloride solution[J]. APPLIED SURFACE SCIENCE,2019,467:1104-1112.
APA	Hou Qiang,Liu Zhiyong,Li Chengtao,Li Xiaogang,&Shao Jiamin.(2019).Degradation of the oxide film formed on Alloy 690TT in a high-temperature chloride solution.APPLIED SURFACE SCIENCE,467,1104-1112.
MLA	Hou Qiang,et al."Degradation of the oxide film formed on Alloy 690TT in a high-temperature chloride solution".APPLIED SURFACE SCIENCE 467(2019):1104-1112.