The Effect of the Thickness of Fe2 Al5 Phase Layer at Fe/Al Interface on the Mechanics Behavior of Hot Dip Aluminizing Coating | |
Chen L; Chen L; Chen L; Chen L; Chen L; Xia Y(夏原); Chen L; Chen L; Chen L; Chen L | |
2004-10-29 | |
会议名称 | 4th International Conference on Surface Engineering, 2004-10-29, |
通讯作者 | 夏原 |
中文摘要 | Hot Dip Aluminized Coatings with different thickness were prepared on Q235 steel in aluminum solutions with different temperature for certain time. Through tensile tests and in-situ SEM observations, the effect of the coating's microstructure on the tensile strength of the samples was studied. It was disclosed at certain aluminum solution temperature,transaction layers mainly composed of Fe2 Al5 phase got thicker with time prolonging, and this changed initial crack's extending direction from parallel with to vertical with stretching direction. The change in crack direction decreased tensile strength of samples, thus made the coating easy to break. It was concluded that the existence of thick Fe2 Al5 phase layer was the basic reason for the lowering of tensile strength of the coating. |
会议录 | Materials Protection,2004,37(z2):158-159 |
学科主题 | 力学 |
内容类型 | 会议论文 |
源URL | [http://dspace.imech.ac.cn/handle/311007/13911] |
专题 | 力学研究所_力学所知识产出(1956-2008) |
通讯作者 | Xia Y(夏原) |
推荐引用方式 GB/T 7714 | Chen L,Chen L,Chen L,et al. The Effect of the Thickness of Fe2 Al5 Phase Layer at Fe/Al Interface on the Mechanics Behavior of Hot Dip Aluminizing Coating[C]. 见:4th International Conference on Surface Engineering, 2004-10-29,. |