Stress singularity analysis at crack tip on bi-material interfaces based on Hamiltonian principle | |
Zhang, HW; Zhong, WX; Li, YP | |
刊名 | ACTA MECHANICA SOLIDA SINICA
![]() |
1996 | |
卷号 | 9页码:124-138 |
关键词 | interface crack fracture mechanics Hamiltonian principle |
ISSN号 | 0894-9166 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/6525705 |
专题 | 大连理工大学 |
作者单位 | DALIAN UNIV TECHNOL,RES INST ENGN MECH,DALIAN 116023,PEOPLES R CHINA. |
推荐引用方式 GB/T 7714 | Zhang, HW,Zhong, WX,Li, YP. Stress singularity analysis at crack tip on bi-material interfaces based on Hamiltonian principle[J]. ACTA MECHANICA SOLIDA SINICA,1996,9:124-138. |
APA | Zhang, HW,Zhong, WX,&Li, YP.(1996).Stress singularity analysis at crack tip on bi-material interfaces based on Hamiltonian principle.ACTA MECHANICA SOLIDA SINICA,9,124-138. |
MLA | Zhang, HW,et al."Stress singularity analysis at crack tip on bi-material interfaces based on Hamiltonian principle".ACTA MECHANICA SOLIDA SINICA 9(1996):124-138. |