Molten salt synthesis and luminescent properties of YVO4:Eu nanocrystalline phosphors | |
Wang F ; Liu CL ; Zhou ZQ ; Jia PY ; Lin J | |
刊名 | journal of rare earths |
2012 | |
卷号 | 30期号:3页码:202-204 |
关键词 | ENERGY-TRANSFER NANOSTRUCTURES NANOPARTICLES SIZE EU LN |
ISSN号 | 1002-0721 |
通讯作者 | jia py |
中文摘要 | yvo4:eu nanocrystalline phosphors were successfully prepared at 400 degrees c in equal moles of nano3 and kno3 molten salts. naoh concentration and annealing temperature played important roles in phase purity and crystallinity of the nanocrystallines, and the optimum naoh concentration and annealing temperature were 6:40 and 400 degrees c, respectively. the nanocrystallines were well crystallized with a cubic morphology in an average grain size of 18 nm. upon excitation of the vanadate groups at 314 nm, yvo4:eu nanocrystallines exhibited the characteristic emission of eu3+, which indicated that there was an energy transfer from vanadate groups to eu3+. moreover, the influence of superficial effect, especially the dangling bonds on the structure and luminescent properties of the nanocrystallines was discussed in detail. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000302991900003 |
公开日期 | 2013-06-08 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/48285] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Wang F,Liu CL,Zhou ZQ,et al. Molten salt synthesis and luminescent properties of YVO4:Eu nanocrystalline phosphors[J]. journal of rare earths,2012,30(3):202-204. |
APA | Wang F,Liu CL,Zhou ZQ,Jia PY,&Lin J.(2012).Molten salt synthesis and luminescent properties of YVO4:Eu nanocrystalline phosphors.journal of rare earths,30(3),202-204. |
MLA | Wang F,et al."Molten salt synthesis and luminescent properties of YVO4:Eu nanocrystalline phosphors".journal of rare earths 30.3(2012):202-204. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论