K3B6O10Br非线性光学晶体的生长及性质研究 | |
张敏; 潘世烈![]() ![]() | |
刊名 | 人工晶体学报
![]() |
2012 | |
卷号 | 41期号:增刊页码:171-174 |
关键词 | K3B6O10Br 非线性光学晶体 晶体生长 光学性质 |
ISSN号 | 1000-985X |
中文摘要 | 采用顶部籽晶法,KF.2H2O-PbO复合助熔剂生长K3B6O10Br晶体,获得了18 mm×18 mm×10 mm尺寸的单晶。K3B6O10Br紫外透过截止边约为210 nm,粉末倍频效应为3倍KDP,利用德拜公式计算了阴离子基团的偶极矩。采用直角棱镜法测试了晶体折射率并拟合了Sellmeier方程。计算及实验表明,K3B6O10Br能够实现532 nm及355 nm倍频输出。对晶体的激光损伤阈值、硬度及潮解性进行了测试。 |
英文摘要 | High quality K3B6O10Br single crystal with size up to 18 mm × 18 mm × 10 mm was obtained via top-seeded solution growth ( TSSG) method using KF·2H2O-PbO binary fluxes. The experiments show that the UV transmission cut off of K3B6O10 Br is about 210 nm. Nonlinear optical measurements demonstrate that the material has second harmonic generation ( SHG) properties,with efficiency approximately three times that of KH2PO4 . The refractive index was test and fit the Sellmeier equation. SHG experiment indicates that the K3B6O10 Br can achieve 532 nm and 355 nm frequency-doubled wavelength. The damage threshold,hardness and deliquescence were reported. |
收录类别 | EI |
公开日期 | 2013-05-16 |
内容类型 | 期刊论文 |
源URL | [http://ir.xjipc.cas.cn/handle/365002/2433] ![]() |
专题 | 新疆理化技术研究所_新疆维吾尔自治区电子信息材料与器件重点实验室 新疆理化技术研究所_材料物理与化学研究室 |
作者单位 | 中国科学院新疆理化技术研究所;新疆电子信息材料与器件重点实验室;中科院研究生院 |
推荐引用方式 GB/T 7714 | 张敏,潘世烈,王颖,等. K3B6O10Br非线性光学晶体的生长及性质研究[J]. 人工晶体学报,2012,41(增刊):171-174. |
APA | 张敏,潘世烈,王颖,杨云,&张方方.(2012).K3B6O10Br非线性光学晶体的生长及性质研究.人工晶体学报,41(增刊),171-174. |
MLA | 张敏,et al."K3B6O10Br非线性光学晶体的生长及性质研究".人工晶体学报 41.增刊(2012):171-174. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论